The invention discloses a cement containing high titanium type blast furnace slag expanding beads, which belongs to the field of building materials. A kind of cement containing high titanium blast furnace slag, which contains the following quality components: 20~100 Portland cement clinker, high titanium type blast furnace slag expansion bead: 10~30 parts, limestone: 5~20, gypsum: 5~10. The invention adopts high titanium blast furnace slag swelling bead made of high titanium blast furnace slag from waste resources to prepare cement. The cement has excellent physical properties. The invention is a green project which is advocated and is worth popularizing for the reuse of high titanium blast furnace slag of abandoned resources.
【技术实现步骤摘要】
一种含有高钛型高炉渣膨珠的水泥
本专利技术属于建材领域,具体涉及一种含有高钛型高炉渣膨珠的水泥。
技术介绍
水泥行业是我国国民经济建设的重要基础材料工业,也是主要的能源资源消耗和污染物排放行业之一。水泥生产行业作为我国主要的高能耗、高排放工业,是产业领域节能减排的重点和难点,其节能减排效果对完成我国能源消耗目标、产业可持续发展起着举足轻重的作用。加大节能减排力度,已成为水泥行业面对的一项艰巨而紧迫的任务。高钛型高炉渣是攀钢普通高炉冶炼钒钛磁铁矿时,产生的熔融矿渣在空气中自然冷却或水冷形成的一种具有一定强度的致密矿渣。与普通高炉渣比,攀钢高炉渣中二氧化钛(TiO2)含量高达20%~24%(由于高钛型高炉渣含钛量高,也称为高钛重矿渣),氧化钙含量较低,即该原料生产的水渣属于非活性材料,因此,攀钢至今有5500多万吨的高钛型高炉渣未被利用,它占地数千亩,而且每年还以300万吨的排渣量增加,攀钢已面临着无处排渣的局面。高钛型高炉渣能否被综合利用,不仅影响到攀钢、攀枝花社会经济的可持续发展,而且对节约自然资源,降低工程成本,保护长江上游生态环境等均具有重要的意义。对于高钛重矿渣的开发利用,有两种不同的技术路线,既提钛利用和不提钛利用。对于提钛利用,虽然是实现高钛重矿渣价值的最理想目标,但由于目前技术制约,利用成本高昂,对高炉渣的消耗也极为有限,提钛后仍然剩余绝大部分渣,因此要解决目前攀钢矿渣大量堆积,占用土地、污染环境的现实问题,当务之急还必须走不提钛利用高钛重矿渣的途径。
技术实现思路
本专利技术要解决的技术问题是提供以高钛型高炉渣为原料的水泥,该水泥更绿色、环保,成 ...
【技术保护点】
含有高钛型高炉渣膨珠的水泥,其特征在于:含有以下质量份的组分:硅酸盐水泥熟料20~100份,高钛型高炉渣膨珠:10~30份,石灰石:5~20份,石膏:5~10份。
【技术特征摘要】
1.含有高钛型高炉渣膨珠的水泥,其特征在于:含有以下质量份的组分:硅酸盐水泥熟料20~100份,高钛型高炉渣膨珠:10~30份,石灰石:5~20份,石膏:5~10份。2.根据权利要求1所述的含有高钛型高炉渣膨珠的水泥,其特征在于:所述高钛型高炉渣膨珠由以下方法制备得到:将高钛型高炉熔渣倾倒入渣沟,流到膨珠槽,然后流到旋转的滚筒上,旋转滚筒叶片将熔渣破碎,然后抛射到空中,向空中运动的渣珠喷水,渣珠形成球形,落入膨珠池,得到高钛型高炉渣膨珠。3.根据权利要求2所述的含有高钛型高炉渣膨珠的水泥,其特征在于:所述高钛型高炉熔渣的温度不小于1000℃。4.根据权利要求2所述的含有高钛型高炉渣膨珠的...
【专利技术属性】
技术研发人员:鲜中菊,杨志远,邓梅艳,蓝静,
申请(专利权)人:攀枝花环业冶金渣开发有限责任公司,
类型:发明
国别省市:四川,51