一种在线用PET‑ITO后制程耐高温承载膜制造技术

本实用新型专利技术涉及一种承载膜，尤其涉及一种可在线用的耐高温承载膜。为了解决现有ITO用耐高温承载膜的耐高温性较差，在高温制程中易翘曲的问题，本实用新型专利技术提供了一种耐高温承载膜。所述承载膜包括PET基材层；所述PET基材层的一侧表面粘接有一层压敏胶层。本实用新型专利技术提供的耐高温承载膜的耐高温性好，翘曲率低。

A line with PET ITO after the process of high temperature resistant bearing

The utility model relates to a bearing film, in particular to a high temperature resistant bearing film for on-line use. In order to solve the problem of the high temperature resistance of the existing ITO high temperature resistant bearing film and the problem of warping in the high-temperature process, the utility model provides a high temperature resistant bearing film. The bearing film includes a PET base layer, and one side of the PET substrate is bonded with a layer of pressure sensitive adhesive layer. The high temperature resistant bearing film provided by the utility model has good high temperature resistance and low warping rate.

【技术实现步骤摘要】
一种在线用PET-ITO后制程耐高温承载膜
本技术涉及一种承载膜，尤其涉及一种可在线用的耐高温承载膜。
技术介绍
PET-ITO膜是指采用磁控溅射技术，在PET基底材料上溅射透明氧化铟锡(ITO)导电薄膜镀层并经高温退火处理得到的高技术产品。由于ITO薄膜材料具有优异的光电特性，因而近年来得以迅速发展，特别是在平板液晶显示、触摸屏等领域得以广泛应用。传统ITO用耐高温承载膜的耐高温性较差，在高温制程中易翘曲。
技术实现思路
为了解决现有ITO用耐高温承载膜的耐高温性较差，在高温制程中易翘曲的问题，本技术提供了一种耐高温承载膜。该耐高温承载膜的耐高温性好，翘曲率低。为了解决上述技术问题，本专利技术提供如下技术方案：本专利技术提供一种耐高温承载膜，所述承载膜包括PET基材层；所述PET基材层的一侧表面粘接有一层压敏胶层。进一步的，所述耐高温承载膜不包括离型层。所述耐高温承载膜用于PET-ITO后制程中在线使用。所述耐高温承载膜也称为可在线用的耐高温承载膜所述压敏胶层的另一侧表面可以与ITO膜的HC面粘接。所述HC面为用户使用时直接面对的面。上述的术语PET-ITO，是指采用磁控溅射技术，在P本文档来自技高网...

【技术保护点】
一种耐高温承载膜，其特征在于，所述承载膜包括PET基材层；所述PET基材层的一侧表面粘接有一层压敏胶层；所述耐高温承载膜不包括离型层；所述PET基材层的厚度为100‑150μm，所述压敏胶层的干膜厚度为8‑12μm，所述压敏胶层采用UV固化型压敏胶。

【技术特征摘要】
1.一种耐高温承载膜，其特征在于，所述承载膜包括PET基材层；所述PET基材层的一侧表面粘接有一层压敏胶层；所述耐高温承载膜不包括离型层；所述PET基材层的厚度为100-150μm，所述压敏胶层的干膜厚度为8-12μm，所述压敏胶层采用U...

【专利技术属性】
技术研发人员：叶国强，董红星，吴传志，郭琰辉，
申请(专利权)人：宁波惠之星新材料科技有限公司，
类型：新型
国别省市：浙江,33