The present invention relates to a method for recovering nickel and cobalt valuable metals from the scrap of a nickel cobalt iron superalloy. The present invention first nickel cobalt iron alloy scrap as anode, the electrochemical capacitance solution way of making liquid, liquid made after iron removal by sodium jarosite method, after removal of iron nickel and cobalt metals co deposition obtained high purity nickel cobalt mixed salt; nickel cobalt iron alloy scrap by high temperature treatment this method not only solves the traditional wet treatment of nickel cobalt iron nickel alloy scrap to dissolve the problem, and the effective recovery of nickel and cobalt in waste of valuable metals.
【技术实现步骤摘要】
一种由镍钴铁高温合金中回收镍钴有价金属的方法
本专利技术涉及一种由镍钴铁高温合金废料中回收镍钴有价金属的方法。
技术介绍
镍钴铁高温合金废料，由于其为纯金属合金，很难用常规湿法冶金处理，而火法工艺由于其能耗高，劳动条件差也未能大规模应用。
技术实现思路
本专利技术的目的是针对现有技术存在的问题提供一种工艺简单、劳动环境好、除杂彻底、能耗及碱耗低的由镍钴铁高温合金废料中回收镍钴有价金属的方法。本专利技术的具体技术方案如下：一种由镍钴铁高温合金废料中回收镍钴有价金属的方法，其特征在于，包括以下步骤：a、将镍钴铁高温合金废料装入网兜中作为阳极，将网兜置于酸性电解液中，用不锈钢板或者钛板做阴极，通入直流电，电流密度在200-1000A/m2，通直流电8-16h，获得镍钴铁的混合电溶液；b、将步骤a中的混合电溶液升温至90-95℃，向其内缓慢加入碳酸钠溶液，调节pH值至2，再加入氧化剂，同时加入碳酸钠溶液，使其pH值稳定在2，搅拌1-2小时后，继续加入碳酸钠至pH值至4，完成除铁；c、在60℃温度下向步骤b中除铁后的混合电溶液中缓慢加入沉淀剂，至pH值为8-9，搅拌1-2小时，...
【技术保护点】
一种由镍钴铁高温合金废料中回收镍钴有价金属的方法，其特征在于，包括以下步骤：a、将镍钴铁高温合金废料装入网兜中作为阳极，将网兜置于酸性电解液中，用不锈钢板或者钛板做阴极，通入直流电，电流密度在200‑1000 A/m
【技术特征摘要】
1.一种由镍钴铁高温合金废料中回收镍钴有价金属的方法，其特征在于，包括以下步骤：a、将镍钴铁高温合金废料装入网兜中作为阳极，将网兜置于酸性电解液中，用不锈钢板或者钛板做阴极，通入直流电，电流密度在200-1000A/m2，通直流电8-16h，获得镍钴铁的混合电溶液；b、将步骤a中的混合电溶液升温至90-95℃，向其内缓慢加入碳酸钠溶液，调节pH值至2，再加入氧化剂，同时加入碳酸钠溶液，使其pH值稳定在2，搅拌1-2小时后，继续加入碳酸钠至pH值至4，完成除铁;c、在60℃温度下向步骤b中除...
【专利技术属性】
技术研发人员：崔海瑞，张恩玉，易超，鲁兴武，
申请(专利权)人：西北矿冶研究院，
类型：发明
国别省市：甘肃,62