The invention belongs to the technical field of wire and cable, the cable is a kind of environmental protection material, comprising by weight of components made of PVC resin 50 PVC 25 80 copies, 35 copies, 15 copies of alumina 10, stearic acid 5 9, adjacent benzene two formic acid two - 6 12, three EPDM 40 60, vinyltrimethoxysilane 1 3 copies, 25 copies of 18 glass fiber, halogen free intumescent flame retardant 20 25 copies, 5 copies of the 3 lubricant, 1 antioxidant 3. The invention adopts PVC resin as the main material, and selects environment-friendly flame retardants, which can greatly reduce the usage of flame retardants, and at the same time, improve the flame retardancy performance, and have the advantages of environmental protection, non-toxic, water absorption and moisture resistance.
【技术实现步骤摘要】
一种环保电缆材料
本专利技术涉及电线电缆
，特别涉及一种环保电缆材料。
技术介绍
现有的国内外耐火电缆主要有氧化镁矿物绝缘防火电缆和云母带绕包无机绝缘的的防火电缆。电线电缆绝缘及护套用塑料俗称电缆料，其中包括了橡胶、塑料、尼龙等多种品种。近几年来,我国电缆料生产企业有了很大的发展,特别是一些民营企业,在生产规模、产品结构调整及新产品开发上顺应市场需求,有很大的提高。但现有技术的电缆料存在阻燃性不够，重金属超标等问题，阻碍了它的应用。可见，现有技术还有待改进和提高。
技术实现思路
鉴于上述现有技术的不足之处，本专利技术的目的在于提供一种环保无害且阻燃性和耐潮性优异的环保电缆材料。为了达到上述目的，本专利技术采取了以下技术方案：一种环保电缆材料，由以下按重量份数计的组分制成：PVC树脂50-80份，聚氯乙烯25-35份，氧化铝粉10-15份，硬脂酸5-9份，邻苯二甲酸二辛酯6-12份，三元乙丙橡胶40-60份，乙烯基三甲氧基硅烷1-3份，玻璃纤维18-25份，无卤膨胀型阻燃剂20-25份，润滑剂3-5份，抗氧剂1-3份。所述的环保电缆材料中，所述组分按照重量份数计算...
【技术保护点】
一种环保电缆材料，其特征在于，由以下按重量份数计的组分制成：PVC树脂50‑80份，聚氯乙烯25‑35份，氧化铝粉10‑15份，硬脂酸5‑9份，邻苯二甲酸二辛酯6‑12份，三元乙丙橡胶40‑60份，乙烯基三甲氧基硅烷1‑3份，玻璃纤维18‑25份，无卤膨胀型阻燃剂20‑25份，润滑剂3‑5份，抗氧剂1‑3份。
【技术特征摘要】
1.一种环保电缆材料，其特征在于，由以下按重量份数计的组分制成：PVC树脂50-80份，聚氯乙烯25-35份，氧化铝粉10-15份，硬脂酸5-9份，邻苯二甲酸二辛酯6-12份，三元乙丙橡胶40-60份，乙烯基三甲氧基硅烷1-3份，玻璃纤维18-25份，无卤膨胀型阻燃剂20-25份，润滑剂3-5份，抗氧剂1-3份。2.根据权利要求1所述的环保电缆材料，其特征在于，所述组分按照重量份数计算为：PVC树脂65...