The present invention relates to a hard bubble polyether polyol and a preparation method for mining grouting material, which belongs to the field of chemical synthesis technology. Ingredients: high degree of initiator, initiator, small molecular additives, amine catalyst and the oxidation of olefins, the mass ratio of 3 20:5 16:1 15:10 5:45 70; the additive for palm oil or paraffin chloride in one or two. The polyether polyol has sufficient compressive strength and has excellent mechanical properties and adhesion, can satisfy the reinforcement, sealing, sealing, filling and other different application requirements of mine grouting material; preparation method of low equipment requirements, the operation is simple and feasible, the product cost has obvious advantages.
【技术实现步骤摘要】
用于矿用注浆料的硬泡聚醚多元醇及制备方法
本专利技术涉及一种用于矿用注浆料的硬泡聚醚多元醇及制备方法，属于化工合成
技术介绍
在众多的高分子矿用加固材料中，聚氨酯加固注浆材料具有质量轻、工艺技术简单、原料配比容易、固化时间可调的优点。但是在聚氨酯加固注浆材料中也出现一些问题，比如反应热高、抗压缩强度不够、阻燃性差、力学性能不足等。为克服现有矿用聚氨酯注浆材料的缺点，研发一种强度高、阻燃性好、反应放热低的新型矿用聚氨酯注浆加固材料十分必要。而聚醚多元醇作为矿用聚氨酯注浆的主要成分之一，其本身特性对矿用聚氨酯注浆料的性能起着至关重要的左右。目前急需要一种反应热低、分子量适中、粘度低、官能度高的聚醚多元醇。
技术实现思路
针对现有技术的不足，本专利技术的目的是提供一种用于矿用注浆料的硬泡聚醚多元醇，具有足够的抗压缩强度而又兼具优异的力学性能和粘结性；同时提供制备方法，操作简单。本专利技术所述的一种用于矿用注浆料的硬泡聚醚多元醇，原料组成为：高官能度起始剂、小分子起始剂、添加剂、胺类催化剂和氧化烯烃，其质量比为3-15:10-20:5-16:1-5:45-70；所述...
【技术保护点】
一种用于矿用注浆料的硬泡聚醚多元醇，其特征在于：原料组成为：高官能度起始剂、小分子起始剂、添加剂、胺类催化剂和氧化烯烃，其质量比为3‑15:10‑20:5‑16:1‑5:45‑70；所述添加剂为棕榈油或氯化石蜡中的一种或两种。
【技术特征摘要】
1.一种用于矿用注浆料的硬泡聚醚多元醇，其特征在于：原料组成为：高官能度起始剂、小分子起始剂、添加剂、胺类催化剂和氧化烯烃，其质量比为3-15:10-20:5-16:1-5:45-70；所述添加剂为棕榈油或氯化石蜡中的一种或两种。2.根据权利要求1所述的用于矿用注浆料的硬泡聚醚多元醇，其特征在于：氯化石蜡为氯化石蜡42或氯化石蜡52中的一种或两种。3.根据权利要求1所述的用于矿用注浆料的硬泡聚醚多元醇，其特征在于：高官能度起始剂为蔗糖或山梨醇中的一种或两种。4.根据权利要求1所述的用于矿用注浆料的硬泡聚醚多元醇，其特征在于：小分子起始剂为甘油、丙二醇、二乙二醇、二丙二醇或水中的一种或多种。5.根据权利要求1所述的用于矿用注浆料的硬泡聚醚多元醇，其特征在于：胺类催化剂为一甲胺、二甲胺、三甲胺或氨水中的一种或多种；氧化烯烃为环氧丙烷或环氧乙烷中的一种或两种。6.一种权利要求1-5任一所述的用于矿用注浆料的硬泡聚醚多元醇的制备方...
【专利技术属性】
技术研发人员：程铸洪，宁晓龙，董卫，白维坤，杨琦，
申请(专利权)人：山东一诺威新材料有限公司，
类型：发明
国别省市：山东,37