玻璃纤维复合钢纸制造技术
Glass fiber composite fiber
Glass fiber composite paper provided by the invention, including steel body, among them, the paper on the outer surface of a glass fiber layer, wherein the glass fiber layer is composed of at least two layers of glass fiber sheet stacking, the glass fiber sheet dislocation adjacent set, the angle formed between the first adjacent to the glass fiber fiber sheet, the angle is 60 degrees, the glass fiber film coated with strengthened layer; the grid component of the glass fiber sheet by the first and two fiber fiber cross woven, between the first fiber and the second fiber inclined intersect to form an included angle beta, the angle beta 35 degrees, the glass fiber composite fiber with high strength, avoid sanding paper curl, improve the flatness of the workpiece grinding, and not easy to absorb water, avoid warping, thereby prolonging the service life.
【技术实现步骤摘要】
玻璃纤维复合钢纸
本专利技术涉及一种钢纸，具体涉及玻璃纤维复合钢纸，属于钢纸磨片的
技术介绍
钢纸又名钢纸磨片，以钢纸为基体，用合成树脂将磨料固结在基体上而制成的片状磨具。钢纸磨片可对金属材料制成的各种复杂型面进行除漆、除锈、除毛刺、磨焊缝等粗加工，广泛应用于制船、航空、机车、桥梁等行业。随着技术的发展，钢纸的质量和性能都有所提高。现有技术中的钢纸包括钢纸本体，所述钢纸本体上固结有磨料，该钢纸柔韧性较差、易破碎、强度差、遇水后容易分解，而且在打磨工件时，由于强度低容易出现卷曲，从而影响工件的打磨质量。
技术实现思路
本专利技术的目的在于，提供一种玻璃纤维复合钢纸，该玻璃纤维复合钢纸强度高，避免打磨时钢纸出现卷曲，提高了工件打磨的平整度，且不容易吸水，避免起翘，从而延长了使用寿命。为了解决以上技术问题，本专利技术提供一种玻璃纤维复合钢纸，包括钢纸本体，其中，所述钢纸本体外表面设有玻璃纤维层，所述玻璃纤维层由至少两层玻璃纤维片叠加而成，相邻的所述玻璃纤维片错位设置，使相邻所述玻璃纤维片的第一纤维之间形成夹角α，所述夹角α为60°，所述玻璃纤维片外包覆强化层；所述...
【技术保护点】
玻璃纤维复合钢纸，包括钢纸本体，其特征在于，所述钢纸本体外表面设有玻璃纤维层，所述玻璃纤维层由至少两层玻璃纤维片叠加而成，相邻的所述玻璃纤维片错位设置，使相邻所述玻璃纤维片的第一纤维之间形成夹角α，所述夹角α为60°，所述玻璃纤维片外包覆强化层；所述玻璃纤维片由第一纤维及第二纤维交叉编织而成的网格状构件，所述第一纤维与所述第二纤维之间倾斜相交以形成夹角β，所述夹角β为35°。
【技术特征摘要】
1.玻璃纤维复合钢纸，包括钢纸本体，其特征在于，所述钢纸本体外表面设有玻璃纤维层，所述玻璃纤维层由至少两层玻璃纤维片叠加而成，相邻的所述玻璃纤维片错位设置，使相邻所述玻璃纤维片的第一纤维之间形成夹角α，所述夹角α为60°，所述玻璃纤维片外包覆强化层；所述玻璃纤维片由第一纤维及第二纤维交叉编织而成...
【专利技术属性】
技术研发人员：郭成祥，
申请(专利权)人：扬中市锋利研磨材料有限公司，
类型：发明
国别省市：江苏,32