The present invention relates to a method of shedding of palladium with activated carbon adsorption of glucose oxidation process, which can effectively solve the problem of glucose oxidation process off the palladium recovery problem, the technical scheme is that the activated carbon is arranged in the container, liquid oxygen, adding sodium gluconate produced in the production process of mixing, static at room temperature filtration, activated carbon filtration, recycling liquid, a return to the container, so repeatedly, until the glucose oxidation process of shedding palladium adsorption on the surface of activated carbon, to achieve the purpose of recovering palladium, or directly used as activated carbon as a carrier of the palladium catalyst is used, the method of the invention is simple, easy to operate, recovery effect well, glucose oxidation process shed a great innovation on the recovery of palladium.
【技术实现步骤摘要】
用活性炭吸附葡萄糖氧化过程中脱落的钯的方法
本专利技术涉及化工领域,特别是一种用活性炭吸附葡萄糖氧化过程中脱落的钯的方法。
技术介绍
在使用多元金属催化剂催化氧化葡萄糖时,由于使用喷射方式反复循环,使活性炭颗粒破碎,致使钯晶粒脱落。据统计,脱落的钯大概占到催化剂中钯的35%,也就是说,催化剂中含有1000g钯,最终收回的钯只有650g,350g钯脱落,按目前市价180元/g计,将损失6.3万元。因此,如何回收损失的钯,是非常值得研究的。要回收葡萄糖氧化时损失的钯,就得搞清楚葡萄糖氧化的过程。在使用多元金属催化剂氧化葡萄糖的过程中,其原理是将葡萄糖溶液加入氧化罐中,再加入多元金属催化剂,利用喷射所产生的负压带入空气,使葡萄糖分子中的醛基氧化成羧基而得到葡萄糖酸。氧化液和催化剂通过泵一起往返循环多次,在这一过程中活性炭被破碎致使钯脱落,这种脱钯方式称为物理脱钯,这就是说钯在葡萄糖氧化液中是以金属单质形式存在,要回收钯于是就有了两种途径,一是采取过滤回收,二是加入某种物质吸附氧化液中的钯,但据有关文献报道,活性炭中微晶钯颗粒直径为2.5nm,要想截留只能采取纳滤,再加上每氧化好一批物料,总体积为3600L左右,纳滤将难以进行。因此,难以普及应用,故开拓新的回收方法势在必行。
技术实现思路
针对上述情况,为克服现有技术的缺陷,本专利技术的目的就是提供一种用活性炭吸附葡萄糖氧化过程中脱落的钯的方法,可有效解决葡萄糖氧化过程中脱落的钯回收问题。本专利技术解决的技术方案是,将活性炭置于容器中,加入葡萄糖酸钠生产过程中产生的氧化液,搅拌均匀,室温下静置,过滤,回收滤液,滤出的 ...
【技术保护点】
一种用活性炭吸附葡萄糖氧化过程中脱落的钯的方法,其特征在于,将50g活性炭置于容器中,加入葡萄糖酸钠生产过程中使用过的氧化液6‑7L,搅拌均匀,室温下静置,过滤,回收滤液,滤出的活性炭再回到容器中,如此反复10次,将葡萄糖氧化过程中脱落的钯吸附在活性炭表面上。
【技术特征摘要】
1.一种用活性炭吸附葡萄糖氧化过程中脱落的钯的方法,其特征在于,将50g活性炭置于容器中,加入葡萄糖酸钠生产过程中使用过的氧化液6-7L,搅拌均匀,室温下静置,过滤,回收滤液,滤出的活性炭再回到容器中,如此反复10次,将葡萄糖氧化过程中脱落的钯吸附...
【专利技术属性】
技术研发人员:李辉,
申请(专利权)人:青岛九洲千和机械有限公司,
类型:发明
国别省市:山东,37