一种多孔纳米饼状结构的ZnO传感电极材料制备方法技术
Preparation of a porous nanoscale ZnO sensing electrode material
A preparation method of a porous nano cake like structure of ZnO sensing electrode belongs to the application technical field of hydrazine hydrate detection. Under the condition of magnetic stirring, two methimidazole (MIM) and zinc acetate (Zn (CH3COO) 2) were mixed to obtain the reaction product. After washing with water and ethanol, centrifugation, solid phase drying and calcination were carried out, and porous nano cake structure ZnO sensing electrode material was obtained. The sensing electrode material of the invention is prepared by magnetic stirring and calcining. The raw materials are environmental protection, abundant reserves, low cost, simple preparation process, easy operation and control, suitable for continuous mass production, and the preparation process is green and environmental friendly.
【技术实现步骤摘要】
一种多孔纳米饼状结构的ZnO传感电极材料制备方法
本专利技术属于电传感检测水合肼应用的
技术介绍
为满足可移动新能源的巨大需求，研制出性能优异、安全价廉、环境友好且催化性能优异的电传感电极材料已引起相关企业和业内专家的广泛关注。当前拥有特殊的物理和化学性质，纳米材料已经被广泛应用于化学传感器、生物传感器等领域。氧化锌材料近年来迅速出现，与大多数贵金属相比，它们价格低廉储量丰富。与此同时，它们有能力促进电子转移反应和提供具有良好的电化学活性。最近，已有关于金属氧化物用于电催化的报道。纳米ZnO是具有六方纤锌矿结构的直接带隙半导体材料，其粒子反应速度是普通ZnO粒子的100～1000倍，具有较大的比表面积，被认为是极具应用前景的高活性电催化材料之一，在电化学检测环境中备受关注。但纳米ZnO修饰的玻碳电极体在水合肼大浓度范围检测中的不稳定性，在工作浓度范围内不能很好的符合电流-浓度的线性关系，严重限制其应用。大量文献报道，采用氮元素掺杂等方法能降低ZnO在动力学上降低反应能级，有效提高其电催化效率，因此，近年来，通过对纳米材料进行氮掺杂，以提高纳米材料的应用性...
【技术保护点】
一种多孔纳米饼状结构的ZnO传感电极材料制备方法，其特征在于在磁力搅拌条件下，将二甲基咪唑和醋酸锌混合反应，取得反应生成物，用水和乙醇洗涤后离心，取固相干燥后煅烧，即得多孔纳米饼状结构的ZnO传感电极材料。
【技术特征摘要】
1.一种多孔纳米饼状结构的ZnO传感电极材料制备方法，其特征在于在磁力搅拌条件下，将二甲基咪唑和醋酸锌混合反应，取得反应生成物，用水和乙醇洗涤后离心，取固相干燥后煅烧，即得多孔纳米饼状结构的ZnO传感电极材料。2.根据权利要求1所述的制备方法，其特征在于所述二甲基咪唑和醋酸锌的投料摩尔比为6∶5。3.根据权利要求2所述的制备方法，其特征在于：将二甲基咪唑水溶液滴加于醋酸锌水溶液中，磁力搅拌条件下反应。4...