一种MOX用二氧化钚原料预处理方法技术

一种MOX用二氧化钚原料预处理方法，包括：选取氧化钚原料、选择相应的烧结舟、将二氧化钚原料均匀平铺至步骤二的烧结舟中、以0.4～23.4L/h的速度对煅烧炉内通入Ar‑1％H2～Ar‑10％H2的干燥空气、将煅烧炉内的温度，以3～21℃/min的升温速率缓慢升温至45～200℃，保温1～48h、以3～20℃/min的速率将煅烧炉降至室温。技术简单，易实现，能够安全可靠的应用到MOX用二氧化钚原料预处理中。

A pretreatment method for two plutonium oxide raw materials for MOX

Including two plutonium oxide raw material pretreatment method, using a MOX: selection of raw materials, selection of plutonium oxide sintering boat, the corresponding two plutonium oxide raw material evenly to two steps sintering boat in 0.4 ~ 23.4L/h, the speed of the calcining furnace into Ar 1%H2 ~ Ar 10%H2 dry air, the calcining furnace temperature to 3~21 DEG /min, the heating rate of slow heating to 45~200 DEG C, holding 1 ~ 48h, at a rate of 3~20 DEG /min will calcination furnace to room temperature. The technology is simple and easy to be realized, and it can be applied safely and reliably to the pretreatment of two plutonium oxide raw materials in MOX.

【技术实现步骤摘要】
一种MOX用二氧化钚原料预处理方法
该技术属于原料预处理领域，具体涉及一种MOX用二氧化钚原料预处理方法。
技术介绍
MOX用二氧化钚原料长时间暴露在大气中，会使钚氧化物颗粒中的可挥发性杂质增加，影响物料配置的准确性，由于水分的存在，导致物料粘性增大，影响球磨、混料处理效果，部分具有还原性的杂质在烧结过程中反应形成还原性杂质气体，会阻碍烧结过程，因此，需要严格控制原料二氧化钚粉末中的可挥发性杂质的含量。氧金属比是MOX燃料最重要的性能指标之一，对MOX燃料的熔点，晶格常数、扩散系数等性能均有较大的影响，按照MOX燃料技术要求，需控制二氧化钚粉末氧金属比在1.95～2.00范围内。目前，传统行业的原料预处理技术主要存在三点不足，一是对温度的控制不适用于钚氧化物处理过程，会导致可挥发性杂质去除不完全，并会使球磨性和烧结性的降低，影响后续制备工艺；二是气氛控制不当导致钚氧化物氧化不充分，氧金属比满足不了1.95～2.00的要求；三是不能满足核物料处理过程中临界、辐射防护要求。为了解决这些问题，本专利设计了一种MOX用二氧化钚原料预处理方法，通过设置合理的加热温度，解决可挥发性杂质去除不完全本文档来自技高网...

【技术保护点】
一种MOX用二氧化钚原料预处理方法，其特征在于：包括以下步骤：步骤一：选取钚含量81～88％，杂质含量1000～13000μg/gPu，水含量0.02～1.21％，水蒸气以外气体含量0.02～0.85％，氧金属比1.90～2.0，比表面积3.2～32m

【技术特征摘要】
1.一种MOX用二氧化钚原料预处理方法，其特征在于：包括以下步骤：步骤一：选取钚含量81～88％，杂质含量1000～13000μg/gPu，水含量0.02～1.21％，水蒸气以外气体含量0.02～0.85％，氧金属比1.90～2.0，比表面积3.2～32m2/g，粒度为3.6～53.2μm，最大直径10.1～98.9μm的二氧化钚原料；步骤二：根据所需处理二氧化钚原料的量与煅烧炉内空间，选择相应的烧结舟；步骤三：将步骤一中的二氧化钚原料均匀平铺至步骤二的烧结舟中，平铺厚度为0.3～5.3cm；步骤四：以0.3～25.1L/...