The invention relates to an anti-corrosion pipeline, the preparation method is as follows: 60 polyurethane 90 copies, 30 copies, 20 toluenediisocyanate three 15 20 hydroxy polyether mixing, stirring time is 20 40min; after adding quartz powder 11 - 15 copies, 6 copies of 4 zinc phosphate mixed together 15 20min, mixed after heating 20min, heated to 60 degrees; heating after adding talcum powder 3 6 copies, 10 copies, 5 barium sulfate castor oil 1 2 copies, 3 copies of zinc powder 2, while maintaining a temperature of 50 degrees of mixing, stirring 30min. The improved formula has strong anticorrosion performance. The coating prepared by this kind of technology is coated outside the pipe, and the anticorrosion effect can be kept for ten years.
【技术实现步骤摘要】
一种防腐管道
本专利技术特别涉及一种防腐管道。
技术介绍
近年来，随着我国石油化工业的迅速发展及城市公用设施建设速度的提高，我国地下金属管道的建设也在飞速的发展。由于地下管道大部分都是金属材质，在土壤和细菌等因素作用下很容易受到腐蚀。地下管道腐蚀给人类和社会环境会带来巨大的经济损失和社会安全，因此新管道的建设和已有管道的维护，给防腐工程提出了重要的任务。
技术实现思路
本专利技术针对上述问题提出了一种防腐管道。具体的技术方案如下：一种防腐管道，其特征在于，制备方法如下：将聚氨酯60-90份、甲苯二异氰酸酯20-30份、三羟基聚醚15-20份进行搅拌混合，搅拌时间为20-40min；之后在加入石英粉11—15份、磷酸锌4-6份搅拌混合15-20min，混合结束后加热20min，加热至60度；加热结束后加入滑石粉3-6份、硫酸钡5-10份、蓖麻油1-2份、锌粉2-3份，保持温度50度的同时进行混合搅拌，搅拌30min。一种防腐管道，其特征在于，所述聚氨酯与甲苯二异氰酸酯质量比例为3:1。一种防腐管道，其特征在于，所述石英粉目数为150目。本专利技术的有益效果为：本专利技术改良配方，具有很强的防腐性能，采用该种工艺制备出的涂料涂覆在管道外，防腐效果可保持十年之久。具体实施方式为使本专利技术的技术方案更加清晰明确，下面对本专利技术进行进一步描述，任何对本专利技术技术方案的技术特征进行等价替换和常规推理得出的方案均落入本专利技术保护范围。实施例1一种防腐管道，其特征在于，制备方法如下：将聚氨酯60份、甲苯二异氰酸酯20份、三羟基聚醚15份进行搅拌混合，搅拌时间为20mi...
【技术保护点】
一种防腐管道，其特征在于，制备方法如下：将聚氨酯60‑90份、甲苯二异氰酸酯20‑30份、三羟基聚醚15‑20份进行搅拌混合，搅拌时间为20‑40min；之后在加入石英粉11—15份、磷酸锌4‑6份搅拌混合15‑20min，混合结束后加热20min，加热至60度；加热结束后加入滑石粉3‑6份、硫酸钡5‑10份、蓖麻油1‑2份、锌粉2‑3份，保持温度50度的同时进行混合搅拌，搅拌30min。
【技术特征摘要】
1.一种防腐管道，其特征在于，制备方法如下：将聚氨酯60-90份、甲苯二异氰酸酯20-30份、三羟基聚醚15-20份进行搅拌混合，搅拌时间为20-40min；之后在加入石英粉11—15份、磷酸锌4-6份搅拌混合15-20min，混合结束后加热20min，加热至60度；加热结束后...
【专利技术属性】
技术研发人员：姜剑波，辛世花，
申请(专利权)人：镇江市星耀智能装备有限公司，
类型：发明
国别省市：江苏,32