A preparation method for high performance fireproof packing

The invention discloses a preparation method of high performance fireproof filler, which is characterized in that the 15 copies and 10 copies of polystyrene polyvinyl alcohol in a reaction kettle for stirring, stirring time 20min, stirring temperature is 60 degrees; adding glass fiber 10 continuous stirring, stirring time 10min, stirring temperature is 44 degrees; finally adding carbonate calcium 6 stirring 20min, stirring temperature is 50 degrees. The raw material of the invention is reasonable, the raw material is cheap and easy to get, the toughness, the plasticity and the fire resistance of the product are improved, the raw material is easy to be obtained, the price is low, and the processing is simple.

【技术实现步骤摘要】
一种高性能防火填料的制备方法
本专利技术涉及一种建筑材料，特别涉及一种高性能防火填料的制备方法。
技术介绍
近年来随着建筑行业的飞速发展，火灾的防控也面临巨大的挑战，防火的重要性不言而喻，防火填料作为最有效的防火材料，可以对火势进行有效的阻燃，防止进一步蔓延，可以有效的减少火灾对人民生命和财产造成的威胁。
技术实现思路
本专利技术针对上述问题提出了一种高性能防火填料的制备方法。具体的技术方案如下：一种高性能防火填料的制备方法，其特征在于，将聚乙烯醇15-25份与聚苯乙烯10-20份放入反应釜中搅拌，搅拌时间为20-40min，搅拌温度为60度；再加入玻璃纤维10-30份搅拌，搅拌时间为10min，搅拌温度为44度；最后加入碳酸钙6-8份搅拌20min，搅拌温度为50度。上述一种高性能防火填料的制备方法，其特征在于，玻璃纤维目数为300目。本专利技术的有益效果为：本专利技术原料配比合理，原料价廉且易得，提高产品韧性、可塑性和防火性，原料易得，价格低廉，加工简单。具体实施方式为使本专利技术的技术方案更加清晰明确，下面对本专利技术进行进一步描述，任何对本专利技术技术方案的技术特征进行等价替换和本文档来自技高网...

【技术保护点】
一种高性能防火填料的制备方法，其特征在于，将聚乙烯醇15份与聚苯乙烯10份放入反应釜中搅拌，搅拌时间为20min，搅拌温度为60度；再加入玻璃纤维10份搅拌，搅拌时间为10min，搅拌温度为44度；最后加入碳酸钙6份搅拌20min，搅拌温度为50度。

【技术特征摘要】
1.一种高性能防火填料的制备方法，其特征在于，将聚乙烯醇15份与聚苯乙烯10份放入反应釜中搅拌，搅拌时间为20min，搅拌温度为60度；再加入玻璃纤维10份搅拌，搅拌时间...