一种ZSM‑22分子筛的制备方法技术
A preparation method of ZSM 22 molecular sieve
The invention discloses a preparation method of ZSM 22 molecular sieve, which comprises the following steps: 1. [BMIm]Cl or [EMIm]Cl dissolved in deionized water, then adding ammonium fluoride in intense mixing process, until transparent solution; (II aluminate and silica sol) into the transparent solution under intensive stirring for 5 minutes. After the crystallization gel; gel 18~42h at 180 DEG C, drying, and calcining at 850 5h, which was ZSM 22 molecular sieve. The invention takes 1, 3 alkyl imidazole ionic liquid as a structure directing agent in various crystallization conditions in 24h synthesis, ZSM prepared by this method 22 molecular sieve with high crystallinity.
【技术实现步骤摘要】
一种ZSM-22分子筛的制备方法
本专利技术属于分子筛催化剂
，特别是涉及ZSM-22分子筛制备方法。
技术介绍
结晶微孔分子筛最初被发现是天然存在的结晶硅铝酸盐矿物，已经成功在实验室中合成并在汽油化工和精细化工行业作为多相催化剂被商业利用。ZSM-22（TON框架）是具有中等孔隙的高硅分子筛，孔径尺寸由5,6和10环组成，其孔系是线性一维与10元环开口。ZSM-22的孔径尺寸约为0.45×0.55nm，小于均具有10元环孔道的ZSM-11和ZSM-5。ZSM-22首先由Dwyer在水热系统中合成包括二乙胺盐酸盐，氢氧化钠，二氧化硅，和硫酸铝。之后，ZSM-22成功使用1,8-辛二胺作为有机结构导向剂在水热系统中合成。目前，ZSM-22的典型合成采用1,6-己二氨作为有机结构导向剂。ZSM-22已被开发用作各种工业应用的有效催化剂，如加氢异构化，选择性催化裂化和甲醇转化为烃。近十年来，离子液体被广泛应用于结构导向剂合成分子筛。具有MFI，BEA，FAU和ANA拓扑结构的分子筛已经成功使用离子液体和咪唑衍生的离子液体作为有机结构导向剂可以在结构上合成所需要结构...
【技术保护点】
一种ZSM‑22分子筛的制备方法，其特征在于包括以下步骤：①将[BMIm]Cl或[EMIm]Cl溶解于去离子水中，然后在剧烈搅拌过程中加入氟化铵，直到得到透明溶液；②硅溶胶在剧烈的搅拌下加入上述透明溶液，5分钟后得到凝胶；③将凝胶在180℃下晶化18~42h，烘干，750~950℃焙烧5h，即得ZSM‑22分子筛。
【技术特征摘要】
1.一种ZSM-22分子筛的制备方法，其特征在于包括以下步骤：①将[BMIm]Cl或[EMIm]Cl溶解于去离子水中，然后在剧烈搅拌过程中加入氟化铵，直到得到透明溶液；②硅溶胶在剧烈的搅拌下加入上述透明溶液，5分钟后得到凝胶；③将凝胶在180℃下晶化18~42h，烘干，750~950℃焙烧5h，即得ZSM-22分子筛。2.如权利要求1所述ZSM-22分子筛的制备方法，其特征在于：步骤②中所得凝胶摩尔成分是SiO2:x[BMIm]Cl或[EMIm]Cl:yNH4F:（25~35）H2O，x为0.5~0.9，y为0.5~0.9。3.一种ZSM-22分子筛的制备方法，其特征在于包括以下步骤：①将[BMIm]C...