The invention discloses a waterproof material and method for foaming wallpaper preparation method, wherein the preparation method comprises the following steps: 1) the nano titanium dioxide, nano calcium carbonate and surfactant mixed and prepared mixture of M1; 2) the mixture of M1 and sodium fatty acid mixture, prepared in a mixture of M2; 3) the presence of solvent, the mixture of M2 and straw mixed powder and hydroxypropyl cellulose, and then drying and grinding, the powders of M3; 4) at the temperature of 220 DEG C 280 under the condition of the molten state, PVC filler, foaming agent and step 3) in the powder mixed M3 system have waterproof material with foaming wallpaper. Through the above design, a good waterproof effect has been achieved.
【技术实现步骤摘要】
发泡墙纸用防水材料及其制备方法
本专利技术涉及墙纸材料领域，具体地，涉及发泡墙纸用防水材料及其制备方法。
技术介绍
发泡墙纸以其多变的花形和较为安全的使用性能而越来越受到人们的欢迎。其相比于涂料具有更安全的使用性能，但是在实际使用时，其也具有一定的局限性，例如，容易被水等浸渍，导致使用性能的降低甚至是损毁等问题。因此，提供一种能使墙纸具有较好的防水性，大大提高其使用性能的发泡墙纸用防水材料及其制备方法是本专利技术亟需解决的问题。
技术实现思路
针对上述现有技术，本专利技术的目的在于克服现有技术中墙纸在实际使用时容易被水等浸渍，导致使用性能的降低甚至是损毁等问题，从而提供一种能使墙纸具有较好的防水性，大大提高其使用性能的发泡墙纸用防水材料及其制备方法。为了实现上述目的，本专利技术提供了一种发泡墙纸用防水材料的制备方法，其中，所述制备方法包括：1)将纳米二氧化钛、纳米碳酸钙和表面活性剂混合，制得混合物M1；2)将混合物M1与脂肪酸钠混合，制得混合物M2；3)在溶剂存在的条件下，将混合物M2与秸秆粉末和羟丙基纤维素混合，而后经干燥研磨，制得粉末M3；4)在温度为220-28...
【技术保护点】
一种发泡墙纸用防水材料的制备方法，其特征在于，所述制备方法包括：1)将纳米二氧化钛、纳米碳酸钙和表面活性剂混合，制得混合物M1；2)将混合物M1与脂肪酸钠混合，制得混合物M2；3)在溶剂存在的条件下，将混合物M2与秸秆粉末和羟丙基纤维素混合，而后经干燥研磨，制得粉末M3；4)在温度为220‑280℃的条件下，将熔融状态的聚氯乙烯、填料、发泡剂和步骤3)中制得的粉末M3混合，制得发泡墙纸用防水材料。
【技术特征摘要】
1.一种发泡墙纸用防水材料的制备方法，其特征在于，所述制备方法包括：1)将纳米二氧化钛、纳米碳酸钙和表面活性剂混合，制得混合物M1；2)将混合物M1与脂肪酸钠混合，制得混合物M2；3)在溶剂存在的条件下，将混合物M2与秸秆粉末和羟丙基纤维素混合，而后经干燥研磨，制得粉末M3；4)在温度为220-280℃的条件下，将熔融状态的聚氯乙烯、填料、发泡剂和步骤3)中制得的粉末M3混合，制得发泡墙纸用防水材料。2.根据权利要求1所述的制备方法，其中，步骤1)中，相对于10重量份的所述纳米二氧化钛，所述纳米碳酸钙的用量为3-5重量份，所述表面活性剂的用量为20-30重量份。3.根据权利要求1或2所述的制备方法，其中，步骤1)中，所述表面活性剂选自十二烷基苯磺酸钠和/或吐温80。4.根据权利要求1或2所述的制备方法，其中，步骤2)中，相对于10重量份的所述混合物M...
【专利技术属性】
技术研发人员：凌清明，周玉斌，吴中建，莫秀斌，
申请(专利权)人：安徽银兔装饰材料有限公司，
类型：发明
国别省市：安徽,34