The invention relates to a method of using converter silicon alloy deoxidation production of low silicon aluminum killed steel, ferrosilicon and silicon manganese alloy by using converter deoxidization production of low silicon aluminum killed steel, ferrosilicon and silicon manganese alloy with LF alloy furnace improvement scheme, process optimization, LF furnace desulfurization process. Changing the production of low silicon aluminum killed steel in converter is a semi boiling tapping way, which reduces the risk of casting machine floc flow, greatly reduces the cost of deoxidizing alloy, reduces the quality risk and reduces the labor intensity of workers, so as to prevent spatter from happening and avoid production accidents.
【技术实现步骤摘要】
一种转炉采用硅系合金脱氧生产低硅铝镇静钢的方法
本专利技术涉及冶金
，尤其涉及炼钢低硅铝镇静钢生产工艺。
技术介绍
Si＜0.03％的含铝镇静钢为低硅铝镇静钢，炼钢领域目前在生产低硅铝镇静钢通常采用常规生产工艺：转炉出钢过程铝系合金预脱氧→LF炉顶渣改质、钢水终脱氧、钢水钙处理→铸机，整个生产工艺过程严禁使用硅系合金。存在的问题是：(1)脱氧铝收得率失衡，终产品Al2O3含量高，铸机絮流几率大，质量风险高；(2)铝系合金用量大，合金成本高。本方法针对以上问题，结合硅镇静钢生产工艺，提出新的脱氧工艺，即转炉出钢过程部分硅系合金预脱氧→LF炉顶渣改质、钢水终脱氧、钢水钙处理→铸机。炼钢领域目前均采用转炉出钢过程铝系合金预脱氧→LF炉顶渣改质、钢水终脱氧、钢水钙处理→铸机，整个生产工艺过程严禁使用硅系合金。存在脱氧铝合金收得率失衡，终产品Al2O3含量高，铸机絮流几率大，质量风险高，铝系合金用量大，合金成本高等诸多问题。
技术实现思路
本专利技术所要解决的技术问题是提供一种转炉采用硅系合金脱氧生产低硅铝镇静钢的方法,改变转炉生产低硅铝镇静钢为半沸腾出钢方式，降低铸机絮...
【技术保护点】
一种转炉采用硅系合金脱氧生产低硅铝镇静钢的方法，其特征在于，具体操作如下：(1)转炉仅加入硅系合金，合金加入量见表1；表1：
【技术特征摘要】
1.一种转炉采用硅系合金脱氧生产低硅铝镇静钢的方法，其特征在于，具体操作如下：(1)转炉仅加入硅系合金，合金加入量见表1；表1：(2)转炉硅系合金加入方式合金准备：料盅合金加入顺序为硅铁合金→硅锰合金；加入时机：出钢至1/3时加入合金及小粒白灰3.70～3.80kg/吨钢；(3)LF炉合金使用采用进LF炉后强吹氩搅拌3～5分钟，强吹氩气流量控制在250～500L/min，保证钢水不发生喷溅现象，根据转炉炉后样的C、S、Si成分的高低，加入铝线段，当该样C＜0.03％，S＞0.04％，Si＜0.015％时，铝线段加入量取上限值，反之取下限值,当顶渣颜色变成绿色时，LF炉过程铝加入，铝线段加入量见表2；表2：钢种铝线段加入量kg/吨钢电石加入量kg/吨钢低硅铝镇静钢1.20～1.410(4)LF炉脱硫工艺1)首批铝脱氧剂加入后立即加入第一批造渣料4～6kg/t钢，白灰:萤石＝4～5:1，强搅拌化渣后将氩气流量调至50～80L/min，根据进站测定温度值和上机时间，确定第1次升温时间，降电极化渣升温，升温...
【专利技术属性】
技术研发人员：王晗桐，姚伟智，梅雪辉，李泽林，臧绍双，许海亮，
申请(专利权)人：鞍钢股份有限公司，
类型：发明
国别省市：辽宁,21