The invention discloses a method for preparing high strength antibacterial UV curing coating, which comprises the following steps: (1) three three trimethylolpropane acrylate, hydroxypropyl methacrylate, first part and a hydroxyalkylbenzophenone mixture; (2) the nano silicon dioxide and nano silver particles with mercaptopropyl methyl two a silane modified mixed with hydroxypropyl methacrylate; then the step (1) and step (2) liquid obtained by mixing, adding two lauric acid two butyl tin and isophorone diisocyanate, sodium chloride to obtain the high strength antibacterial light curing coating. The UV curable coating prepared by the invention has no oxygen resistance, full curing, excellent mechanical properties and antibacterial effect at the same time.
【技术实现步骤摘要】
一种高强度抗菌光固化涂料的制备方法
本专利技术涉及光固化涂料的领域。
技术介绍
光固化涂料又称光敏涂料，通常是以紫外光为能源，引发涂料组分进行反应得到的涂料，光固化涂料在使用时不需要加热，可在纸张、塑料、皮革和木材等易燃底材上迅速固化成膜，其固化时间短、固化温度低、挥发分低，可节省大量能源、资源，无公害、高效率。但光固化涂料的一个显著缺点是固化过程易出现氧阻效应，导致涂料固化不良，性能受限。
技术实现思路
本专利技术的目的在于提出一种固化优良、性能优异、并且具有抗菌效果的光固化涂料的制备方法。本专利技术的技术方案如下：一种高强度抗菌光固化涂料的制备方法，包括以下步骤：（1）将三羟甲基丙烷三丙烯酸酯、第一部分甲基丙烯酸羟丙酯、及α-羟烷基苯酮在10~20℃下搅拌混合均匀；（2）将纳米二氧化硅与纳米银粒子加入甲苯中，使用超声分散10~30min，其后加入巯丙基甲基二甲氧基硅烷，升温至100~110℃回流30~60min，其后继续升温并浓缩液体至1/4体积，降温至30~40℃时加入第二部分甲基丙烯酸羟丙酯，搅拌均匀；（3）将步骤（1）得到的液体与步骤（2）得到的液体混合，加...
【技术保护点】
一种高强度抗菌光固化涂料的制备方法，其特征在于：包括以下步骤：（1）将三羟甲基丙烷三丙烯酸酯、第一部分甲基丙烯酸羟丙酯、及α‑羟烷基苯酮在10~20℃下搅拌混合均匀；（2）将纳米二氧化硅与纳米银粒子加入甲苯中，使用超声分散10~30min，其后加入巯丙基甲基二甲氧基硅烷，升温至100~110℃回流30~60min，其后继续升温并浓缩液体至1/4体积，降温至30~40℃时加入第二部分甲基丙烯酸羟丙酯，搅拌均匀；（3）将步骤（1）得到的液体与步骤（2）得到的液体混合，加入二月桂酸二丁基锡和异佛尔酮二异氰酸酯，氯化钠搅拌均匀并避光保存，即得到所述高强度抗菌光固化涂料；其中所述纳米...
【技术特征摘要】
1.一种高强度抗菌光固化涂料的制备方法，其特征在于：包括以下步骤：（1）将三羟甲基丙烷三丙烯酸酯、第一部分甲基丙烯酸羟丙酯、及α-羟烷基苯酮在10~20℃下搅拌混合均匀；（2）将纳米二氧化硅与纳米银粒子加入甲苯中，使用超声分散10~30min，其后加入巯丙基甲基二甲氧基硅烷，升温至100~110℃回流30~60min，其后继续升温并浓缩液体至1/4体积，降温至30~40℃时加入第二部分甲基丙烯酸羟丙酯，搅拌均匀；（3）将步骤（1）得到的液体与步骤（2）得到的液体混合，加入二月桂酸二丁基锡和异佛尔酮二异氰酸酯，氯化钠搅拌均匀并避光保存，即得到所述高强度抗菌光固化涂料；其中所述纳米银粒子的粒径为20~30nm。2.根据权利要求1所述的高强度抗菌光固化涂料的制备方法，其特征在于：按质量份计，原料为以下组分：三羟甲基丙...