一种以粉煤灰提铝酸渣、超塑性黏土及油页岩为原料制备超轻质陶粒的工艺制造技术
A process for the preparation of ultralight ceramsite with fly ash aluminate slag, superplastic clay and oil shale as raw materials
The invention discloses a process for extracting aluminum from fly ash acid slag, clay and Superplasticity of oil shale as raw material to prepare ultra light haydite, which is the raw material crushing, grinding, mixing process in accordance with the material two molding sintering, prepared excellent physical and mechanical properties of high expansion super light ceramsite. The finished product super light ceramsite bulk density, apparent density, porosity, cylinder compressive strength and water absorption rate reached 2010 in the national standard GBT17431.2.
【技术实现步骤摘要】
一种以粉煤灰提铝酸渣、超塑性黏土及油页岩为原料制备超轻质陶粒的工艺
本专利技术涉及一种超轻集料陶粒的制备工艺。
技术介绍
陶粒外壳坚硬，且其内部呈细密蜂窝状微孔，具有封闭特征，有利于隔热与隔声，可以用于墙体保温材料。陶粒的性能包括：质量轻、密度低、筒压强度高、孔隙率高、软化系数高、导热性低、抗冻性良好、抗碱集料反应、抗冲击等。由于陶粒密度小、内部多孔、形态和成分均一，具有一定强度和坚固性、耐腐蚀、抗冻、抗震，因此陶粒广泛应用于建材、园艺、食品饮料、耐火保温材料、化工、石油等部门。在陶粒专利技术之初，其作为一种新型轻骨料建筑材料用于建材领域，以陶粒为原料制成的轻骨料混凝土空心砌块、梁、板等已成为实心粘土砖的重要替代品，并发展成为一类新型墙体材料的主导产品。随着技术的不断发展和人们对陶粒性能认识的更加深入，其应用早已超过建材这一范围。目前，陶粒在建材方面的应用已经由100％下降到80％，在其他方面的应用占20％，尤其是随着城市建设的加快，陶粒在园艺、园林方面的应用也越来越广泛。园艺陶粒仍有很大的发展空间，其需求也在逐年增加，我国陶粒在园艺、园林方面的应用量将会逐年上升...
【技术保护点】
一种以粉煤灰提铝酸渣、超塑性黏土及油页岩为原料制备超轻质陶粒的工艺，其特征在于，包括如下步骤：第一步，准备阶段：依次用颚式破碎机和盘式粉磨机将粉煤灰提铝酸渣、超塑性黏土和油页岩生料进行破碎、粉磨，然后过150目筛，分别获得粉煤灰提铝酸渣粉末、超塑性黏土粉末和油页岩粉末；第二步，混料：按照质量比7:7:6，分别称取粉煤灰提铝酸渣粉末、超塑性黏土粉末和油页岩粉末，混合均匀，然后按照灰水比2.0～2.2：1加水搅拌均匀，获得混合料；第三步，成型：将所述混合料放入造粒机中成型，所得样品放入鼓风干燥箱中于105℃下烘干至恒重，获得混合料颗粒；第四步，烧制陶粒：将箱式电阻炉或回转窑预烧...
【技术特征摘要】
1.一种以粉煤灰提铝酸渣、超塑性黏土及油页岩为原料制备超轻质陶粒的工艺，其特征在于，包括如下步骤：第一步，准备阶段：依次用颚式破碎机和盘式粉磨机将粉煤灰提铝酸渣、超塑性黏土和油页岩生料进行破碎、粉磨，然后过150目筛，分别获得粉煤灰提铝酸渣粉末、超塑性黏土粉末和油页岩粉末；第二步，混料：按照质量比7:7:6，分别称取粉煤灰提铝酸渣粉末、超塑性黏土粉末和油页岩粉末，混合均匀，然后按照灰水比2.0～2.2：1加水搅拌均匀，获得混合料；第三步，成型：将所述混合料放入造粒机中成型，所得样品放入鼓风干...