The invention discloses a high surface area ZnMn2O4 preparation method of zinc nitrate, manganese nitrate dissolved in water, then add the right amount of glycine in aqueous solution, stirring dissolved after adding a certain amount of SiO2 in solution in 250 colloid, a temperature of 400 DEG C for heating the reaction mixture until the occurrence of the combustion reaction, after the reaction is finished. The product is then washed with distilled water, 80 degrees in the solid product by etching 24h sodium hydroxide solution; and drying to obtain high surface area ZnMn2O4. The invention adopts the solution combustion method, reaction temperature required is relatively low, only 250 400 DEG C; without adding surfactant, easy batch production, simple process, short production cycle, easy operation; the prepared ZnMn2O4 material has low density, large specific surface area (up to 186.4m
【技术实现步骤摘要】
一种高比表面积ZnMn2O4的制备方法
本专利技术属于纳米材料制造和化工领域，具体为一种高比表面积ZnMn2O4的制备方法。
技术介绍
尖晶石型双金属氧化物是一类重要的无机功能材料，在许多领域如电化学储能、传感器、生物医学和催化等方面都有较为广泛的应用。而其中ZnMn2O4以其丰富的结构和优异的磁、光、电、催化等特性吸引了人们极大的关注。制备尖晶石型氧化物传统的方法是高温煅烧氧化物的混合物，但要维持在较高的温度下反应。近年来，有文献报道了，用水热(溶剂热)法、静电纺丝法、溶胶-凝胶法、固相法、共沉淀等方法制备ZnMn2O4微纳米结构材料，但是这些方法存在工艺过程复杂、工艺条件苛刻、能耗高、生产周期长、产量低等不足，不利于工业化生产。具体地，如下文所述：《无机盐工业》2017年第3期公开了一篇《尖晶石型ZnMn2O4水热合成及光催化性能研究》，论文首先以氯化锰与硝酸锌为原料，尿素作为沉淀剂，在180℃水热反应20h制备前驱体，然后在400℃煅烧前驱体3h，得到浅灰色粉末状ZnMn2O4。该合成路径包含两个步骤，且反应时间较长、能耗较高、产量低。《化工新型材料》201...
【技术保护点】
一种高比表面积ZnMn2O4的制备方法，其特征在于：以硝酸锌、硝酸锰、甘氨酸和二氧化硅胶体溶液为原料进行溶液燃烧反应，反应结束后，经后处理得到高比表面积ZnMn2O4。
【技术特征摘要】
1.一种高比表面积ZnMn2O4的制备方法，其特征在于：以硝酸锌、硝酸锰、甘氨酸和二氧化硅胶体溶液为原料进行溶液燃烧反应，反应结束后，经后处理得到高比表面积ZnMn2O4。2.根据权利要求1所述的高比表面积ZnMn2O4制备方法，其特征在于：所述的燃烧反应引发条件为：在250-400℃的温度下进行加热直至开始燃烧。3.根据权利要求2所述的高比表面积ZnMn2O4制备方法，其特征在于：所述的燃烧反应引发条件为：在300℃的温度下进行加热直至开始燃烧。4.根据权利要求1所述的高比表面积ZnMn2O4的制备方法，其特征在于：所述后处理是将反应后的产物进行固液分离，依次用蒸馏...
【专利技术属性】
技术研发人员：李中春，董安亮，王英，周志豪，许霞，