本发明专利技术提供一种提高钢板点焊飞溅电流的方法，其点焊工艺包括电极加压、预热、焊接、电极保压及移除电极五个过程，在焊接电流之前增加一个预热电流，预热电流为3～4.5kA，预热时间为150～450ms。本发明专利技术可明显提高飞溅电流，扩大点焊工艺范围，提高点焊工艺的稳定性，而且能够增大熔核尺寸，提高焊点拉剪强度，改善焊点质量。所采用的焊接及预热工艺参数在普通点焊机上即可实现，可实现工业应用。

A method to improve the spatter current of steel plate spot welding

The present invention provides a method for improving the welding current of the welding spatter, including electrode pressure, preheating, welding, electrode pressure and removing electrode five processes, an increase in the preheating current welding current before the preheating current is 3 ~ 4.5kA, the preheating time is 150 ~ 450ms. The invention can significantly improve the splashing current, expand the spot welding technology range, improve the stability of spot welding process, and increase the nugget size, improve the tensile strength and the quality of solder joints. The welding and preheating process parameters used can be realized on the ordinary spot welding machine and can be used in industrial application.

【技术实现步骤摘要】
一种提高钢板点焊飞溅电流的方法
本专利技术属于焊接
，具体为一种提高钢板点焊飞溅电流的方法。
技术介绍
随着工业技术的日益发展，点焊作为一种焊接技术，越来越受到焊接界的青睐，点焊能有如此重要的地位，归结于它具有低能耗、低成本、高质量、高效率且便于实现自动化、使用方便等优点。与此同时，焊接自动化的发展为点焊技术的发展提供了广阔的前景，电阻点焊已被广泛应用于汽车白车身的生产过程之中。目前，大多数工业应用及科学研究所使用的点焊工艺均是由电极加压、焊接、电极保压及移除电极四个过程组成，采用此工艺进行钢板焊接，焊接电流范围较小，工艺选择不当可产生点焊飞溅，降低焊点性能，进而降低整个白车身的安全性，因此如何提高点焊飞溅电流，进而扩大点焊工艺范围是点焊研究的一个重要方向。公开号CN201210095247.7提出了一种汽车车身点焊飞溅检测与控制装置及其方法，该方法可以在线检测点焊飞溅，还可以通过对采集的飞溅图像进行处理，得出飞溅特征，并给出飞溅产生的方位，作出质量评判。但该方法并不能提高飞溅电流。公开号CN201220546390.9提供了一种用于钢板点焊定位和防飞溅的装置，解决了点焊试样定本文档来自技高网...

【技术保护点】
一种提高钢板点焊飞溅电流的方法，其特征在于，点焊工艺包括电极加压、预热、焊接、电极保压及移除电极五个过程，在焊接电流之前增加一个预热电流，预热电流为3～4.5kA，预热时间为150～450ms。

【技术特征摘要】
1.一种提高钢板点焊飞溅电流的方法，其特征在于，点焊工艺包括电极加压、预热、焊接、电极保压及移除电...

【专利技术属性】
技术研发人员：魏世同，刘仁东，吕冬，林利，陆晓峰，苏洪英，丁庶炜，徐鑫，郝志强，李萧彤，
申请(专利权)人：鞍钢股份有限公司，
类型：发明
国别省市：辽宁,21