The invention belongs to the field of noble metal catalysts, in particular relates to a method for preparing double metal catalyst for platinum and palladium, palladium and platinum by carbonate carbonate by the dispersing agent are mixed evenly dispersed solid, and the addition of alcohol water mixtures in a sealed pressurized reaction, adding reducing agent and initiator to seal heating reaction, reaction liquid then, the filter after the reaction liquid by using deionized water ultrasonic cleaning by white precipitate to obtain white powder by sintering. The active component of the catalyst prepared by the invention is suitable and evenly distributed, and the activity of the catalyst is high.
【技术实现步骤摘要】
一种铂钯双金属催化剂的制备方法
本专利技术属于贵金属催化剂领域，具体涉及一种铂钯双金属催化剂的制备方法。
技术介绍
铂基催化剂具有优异的催化性能，在环境工程、能源、工业生产等领域起到了重要的作用。例如：汽车尾气的净化，燃料电池的催化，电解水制氢等等。目前，商业Pt/C催化剂已在诸多领域得到了广泛的应用，极大地推动了生产力的发展。然而，铂在地壳中储量十分有限，且价格昂贵成本高，非贵金属的替代品性能较铂差，现有商业Pt/C催化剂中铂纳米颗粒又有易聚集、循环性较差的缺点。因此，如何提高现有铂的催化性能，从而降低铂的使用量，已成为极具意义的课题。在过去的十几年里科研人员已做出了大量的工作，成功的提升了催化剂的性能，主要手段有：1.将铂颗粒细小纳米化而获得高的比表面积；2.调节颗粒的结构形貌，如制备多孔结构，高活性面暴露率，空心笼装结构等；3.制备铂基合金利用合金效应等手段；4.负载剂的选择与调控等等。但是，现有技术中商业Pt/C催化剂的性能仍达不到要求。
技术实现思路
针对现有技术中的问题，本专利技术提供一种铂钯双金属催化剂的制备方法，制备的催化剂活性组分粒径适宜和分布均匀，...
【技术保护点】
一种铂钯双金属催化剂的制备方法，其特征在于：所述制备方法按照如下步骤：步骤1，将碳酸铂与碳酸钯混合搅拌，搅拌均匀后加入分散剂搅拌均匀后，得到混合固体；步骤2，将混合固体加入至反应釜中加入醇水混合物，密封加压反应2‑5h，自然冷却形成悬浊醇液；步骤3，将悬浊醇液中加入还原剂与引发剂，密封加热反应3‑6h；步骤4，将步骤3的反应液进行过滤后采用去离子水超声清洗1‑2次，然后烘干，得到白色沉淀；步骤5，将白色沉淀放入马弗炉中烘干烧结1‑3h，直至变成白色粉体。
【技术特征摘要】
1.一种铂钯双金属催化剂的制备方法，其特征在于：所述制备方法按照如下步骤：步骤1，将碳酸铂与碳酸钯混合搅拌，搅拌均匀后加入分散剂搅拌均匀后，得到混合固体；步骤2，将混合固体加入至反应釜中加入醇水混合物，密封加压反应2-5h，自然冷却形成悬浊醇液；步骤3，将悬浊醇液中加入还原剂与引发剂，密封加热反应3-6h；步骤4，将步骤3的反应液进行过滤后采用去离子水超声清洗1-2次，然后烘干，得到白色沉淀；步骤5，将白色沉淀放入马弗炉中烘干烧结1-3h，直至变成白色粉体。2.根据权利要求1所述的一种铂钯双金属催化剂的制备方法，其特征在于：所述步骤1中的碳酸铂与碳酸钯的摩尔量比例为1:0.3-0.5。3.根据权利要求1所述的一种铂钯双金属催化剂的制备方法，其特征在于：所述步骤1中的分散剂采用聚乙烯吡咯烷酮，分散剂的摩尔量是碳酸铂的15-25％。4.根据权利要求1所述的一种铂钯双金属催化剂的制备方法，其特征在...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。