The invention discloses a method for preparing nickel ammonium sulfate from nickel sulfide ore at atmospheric pressure. In dilute nickel ore, dilute acid, oxidant and calcium sulfate inhibitor are added to mix evenly, and then the nickel sulphate leaching solution is obtained. In the leaching solution, ammonia and limestone were added, and iron was removed by ammonium jarosite process. After the removal of iron, ammonia and ammonium sulfate solution were added to the leaching solution, and impurities were precipitated. The invention has the characteristics of short process, low cost and green environmental protection.
【技术实现步骤摘要】
一种用硫化镍矿常压制备硫酸镍铵的方法
本专利技术涉及硫化镍矿资源化利用领域，具体涉及一种用硫化镍矿常压制备硫酸镍铵的方法。
技术介绍
硫化镍矿的处理工艺一般可分为火法和湿法。火法处理工艺是采用造锍熔炼，将硫化镍矿中的镍熔炼成低镍锍，再将低镍锍用转炉吹炼成高镍锍，再经不同精炼方法生产出不同的镍产品。主要的工艺有硫化镍矿鼓风炉熔炼、电炉熔炼、闪速熔炼和熔池熔炼等。湿法处理工艺一般是指浸出到溶液中的提镍过程，主要的工艺有硫酸化焙烧浸出法、常压氨浸法、加压氨浸法、氧压浸出法和氯化浸出法等。黄铵铁矾的化学式为：NH4Fe3(SO4)2(OH)6，在含铁的硫酸浸出液中，形成黄铵铁矾沉淀，可将溶液中的铁除去，方程式简化如下：3Fe3++NH4++2SO42+6H2O→NH4Fe3(SO4)2(OH)6↓+6H+(1)该方法的特点为：黄铵铁矾晶体容易形成，浸出液容易澄清、过滤和分离，金属(Ni、Cu、Mn)损失低。常压浸出一般是在室温或溶液沸点温度以下进行的工艺，往往浸出速度较慢，浸出的时间较长。将硫化镍矿粉磨成小的颗粒，可增加硫化镍矿与液体的接触面积，增加反应速率。
技术实现思路
...
【技术保护点】
一种用硫化镍矿常压制备硫酸镍铵的方法，其特征在于，包括下述步骤：(1)原料浸出按照重量份计，在100份的硫化镍矿中，加入200‑500份稀酸、40‑60份氧化剂及5‑10份硫酸钙抑制剂，混合均匀后，在60‑90℃，反应1‑6h，得到硫酸镍浸出液；(2)浸出液除杂在浸出液中，加入氨水和石灰石，通过黄铵铁矾法除铁，反应至溶液pH值为2；除铁后的浸出液加入氨水，反应至溶液pH值为11，得到硫酸镍铵溶液和杂质沉淀。
【技术特征摘要】
1.一种用硫化镍矿常压制备硫酸镍铵的方法，其特征在于，包括下述步骤：(1)原料浸出按照重量份计，在100份的硫化镍矿中，加入200-500份稀酸、40-60份氧化剂及5-10份硫酸钙抑制剂，混合均匀后，在60-90℃，反应1-6h，得到硫酸镍浸出液；(2)浸出液除杂在浸出液中，加入氨水和石灰石，通过黄铵铁矾法除铁，反应至溶液pH值为2；除铁后的浸出液加入氨水，反应至溶液pH值为11，得到硫酸镍铵溶液和杂质沉淀。2.如权利要求1所述的一种用硫化镍矿常压制备硫酸...
【专利技术属性】
技术研发人员：谭宏斌，王久维，周旭，马小玲，杨陆海，王进，王军霞，王玉甫，陈建新，张斌，李文海，
申请(专利权)人：西南科技大学，
类型：发明
国别省市：四川,51