The present invention provides a method for mixing plastic granulation particles, which comprises the following steps: A, clean up the mixing tube, the mixing tube wall clean clean up the fat B, Budd Chiari; preliminary mixing, will be 2/3 of the total amount of plastic particles into mixing barrel and adding white wax, mixing 10 15 minutes; C, mixing, preliminary mixing after the completion of first adding good toner, then add the remaining plastic particles, mixing 30 50 minutes. The invention provides a method of mixing plastic granulation particle, the mixing effect is good, especially for a large amount of toner as to avoid mixing the inadequacy of complementary, save cost and increase economic benefits.
【技术实现步骤摘要】
一种塑胶粒子造粒的混料方法
本专利技术涉及一种混料方法，特别涉及一种塑胶粒子造粒的混料方法。
技术介绍
塑胶粒子染色的流程是将塑胶粒子与色粉混合经过押出机重新造粒，前期的混料至关重要，混料的好坏决定了需不需要补色。现有技术中的混料方式较差，尤其是色粉量较大的容易造成混料不均匀。
技术实现思路
【1】要解决的技术问题本专利技术要解决的技术问题是提供一种混料效果好的塑胶粒子造粒混料方法。【2】解决问题的技术方案一种塑胶粒子造粒的混料方法，其特征在于，包括以下步骤：a、清理混料筒，使用干净的布加上去脂油将混料筒内壁擦干净；b、初步混料，将总量三分之二的塑胶粒子加入混料筒并加入适量的白蜡油，混料10-15分钟；c、混料，初步混料完成后先加入称好的色粉，接着加入剩余的塑胶粒子，混料30-50分钟。【3】有益效果本专利技术提供塑胶粒子造粒的混料方法，混料效果好，尤其是对于色粉量较大的避免了因为混料不充分而造成的补色，节约了成本，增加了经济效益。具体实施方式下面详细介绍本专利技术实施例。一种塑胶粒子造粒的混料方法，其特征在于，包括以下步骤：a、清理混料筒，使用干净的布加上去脂油将混料筒内壁擦干净；b、初步混料，将总量三分之二的塑胶粒子加入混料筒并加入适量的白蜡油，混料10-15分钟；c、混料，初步混料完成后先加入称好的色粉，接着加入剩余的塑胶粒子，混料30-50分钟。本专利技术提供塑胶粒子造粒的混料方法，混料效果好，尤其是对于色粉量较大的避免了因为混料不充分而造成的补色，节约了成本，增加了经济效益。以上所述仅是本专利技术的优选实施方式，应当指出，对于本
的普通技术人员...
【技术保护点】
一种塑胶粒子造粒的混料方法，其特征在于，包括以下步骤：a、清理混料筒，使用干净的布加上去脂油将混料筒内壁擦干净；b、初步混料，将总量三分之二的塑胶粒子加入混料筒并加入适量的白蜡油，混料10‑15分钟；c、混料，初步混料完成后先加入称好的色粉，接着加入剩余的塑胶粒子，混料30‑50分钟。
【技术特征摘要】
1.一种塑胶粒子造粒的混料方法，其特征在于，包括以下步骤：a、清理混料筒，使用干净的布加上去脂油将混料筒内壁擦干净；b、初步混料，将总量三分之二...