一种强韧性果胶基复合膜及其制备方法技术

本发明专利技术涉及包装材料技术领域，特别是一种强韧性果胶基复合膜及其制备方法，由重量份数的果胶4%‑10%、明胶1%‑5%、甘油0.5%‑2.5%、邻苯二甲酸二甲酯0%‑2%、柠檬酸三丁酯0.2%‑1%、水79.5%‑94.3%制成，包括以下步骤：步骤一，制备果胶和明胶溶液；步骤二，制备果胶膜溶液；步骤三，超声脱气；步骤四，干燥成膜。本发明专利技术工艺条件温和，方法简便，生产成本低，市场前景广阔。

A strong toughening pectin based composite membrane and its preparation method

The invention relates to the technical field of packaging materials, in particular to a strengthening of pectin composite film and its preparation method, made by the weight of pectin 10%, gelatin 1% 4% 5%, glycerol 0.5% 2.5% phthalate two formic acid and two methyl 0% 2% citric acid, three 1%, 79.5% 0.2% butyl water 94.3%, comprising the following steps: 1. Preparation of pectin and gelatin solution; step two, the preparation of pectin film solution; step three, ultrasonic degassing; step four, dry film. The invention has the advantages of mild process conditions, simple method, low production cost and wide market prospect.

【技术实现步骤摘要】
一种强韧性果胶基复合膜及其制备方法
本专利技术涉及包装材料
，特别是一种强韧性果胶基复合膜。
技术介绍
随着科技的快速发展和社会的进步，包装业的发展也呈现出多元化的发展趋势。目前市场上大部分的包装材料采用难以在自然环境中降解的聚苯乙烯等塑料为基材，大量不可降解、不可回收塑料包装材料的过度使用，不仅造成资源和能源的大量浪费，更对我们赖以生存的生态环境造成了严重危害。由包装材料造成的环境污染已引起了世界各国的广泛关注，世界各国陆续开展易降解、可回收的绿色包装材料的研究开发工作，其中以果胶为基体的复合膜因具有良好的生物降解性能和对人体健康无害性，受到了越来越多消费者的青睐，具有广阔的市场前景。现有果胶保鲜膜制备技术以果胶和其他化工原料（如聚合物等）为主，难以做到真正的绿色环保无污染。例如，申请号为201410026040.3，名称为“一种果胶保鲜膜及其制备方法”专利，所制备的果胶保鲜膜主要成分为果胶和聚乙烯醇；申请号为201210545974.9，名称为“PVA/壳聚糖/果胶共混膜”专利，所制备的果胶共混膜主要成分为聚乙烯醇、壳聚糖和果胶。上述以聚乙烯醇等为主要原料的果胶膜，虽然减轻本文档来自技高网...

【技术保护点】
一种强韧性果胶基复合膜，其特征在于由以下重量百分比的原料制成：果胶4%‑10%、明胶1%‑5%、甘油0.5%‑2.5%、邻苯二甲酸二甲酯0%‑2%、柠檬酸三丁酯0.2%‑1%、水79.5%‑94.3%。

【技术特征摘要】
1.一种强韧性果胶基复合膜，其特征在于由以下重量百分比的原料制成：果胶4%-10%、明胶1%-5%、甘油0.5%-2.5%、邻苯二甲酸二甲酯0%-2%、柠檬酸三丁酯0.2%-1%、水79.5%-94.3%。2.权利要求1所述的强韧性果胶基复合膜的制备方法，其特征在于步骤如下：（1）将果胶和明胶加入到热水中溶解，搅拌反应0.5-2h，得到胶溶液；（2）依次将甘油、邻苯二甲酸二甲酯、柠檬酸三丁酯加入到步骤（1）得到的胶溶液中，在40℃-50℃的条件下搅拌反应10-30min，得到混合溶液；（3）成膜：将步骤（2）中得...

【专利技术属性】
技术研发人员：娄辉清，闫新，王艳，王利娜，高秀丽，盛杰侦，王业涛，李鹏博，
申请(专利权)人：河南工程学院，
类型：发明
国别省市：河南,41