The invention discloses a multi component low vanadium catalyst for preparation of benzol four acid two anhydride by sol-gel method. The main catalyst in the catalyst for V2O5 and TiO2, V:Ti molar ratio of 0.05:1 to 0.15:1; the catalyst, catalyst for B2O3, SnO2 and CeO2 to V, the amount of substance basis 1, which B the amount of substance is 0.001 0.1, Sn molar was 0.001 0.1, Ce the amount of substance is 0.001 0.1, the catalyst carrier of 5 6mm SiC. The method used in the invention is simple and has wide raw materials, and it can prepare large amount of catalyst with fine particle size, good selectivity and low vanadium content. It is suitable for the application of gas phase oxidation of four toluene.
【技术实现步骤摘要】
溶胶法制备均苯四酸二酐的多组分低钒催化剂
本专利技术涉及化学
，具体涉及一种催化剂及其制备方法，尤其是用于制备均苯四酸二酐的催化剂。
技术介绍
目前，均酐的制备方法主要有三种，分别为均四甲苯氧化法、偏三甲苯烷基化法和一氧化碳法。其中工业上使用较为广泛的是均四甲苯气相氧化法，其优点是只需一步即可制得均酐，工艺简单；以空气为氧化剂，可以连续制备，便于工业生产。制备均酐催化剂的常用制备工艺有喷涂法、浸渍法等。一般对均酐催化剂的制备采用喷涂法，以预定比例将各组分混合制成悬浮液备用，然后用喷枪将悬浮液喷涂至载体表面形成一定厚度，最后焙烧活化催化剂。气相催化氧化均四甲苯制取均苯四甲酸二酐所用催化剂目前以V2O5为主催化剂，并辅以其他金属氧化物为助催化剂。邓国才等以V2O5为主，Ti、Nd、P、Cs的氧化物为辅制备出的催化剂在反应温度(460±10)℃、空速6000～8000h-、均四甲苯在空气中的浓度(20±3)g/m3时，固体粗酐的收率可达95％～100％，产品的质量好、副产物少、易于精制提纯。该催化剂具有重现性好、稳定性高、使用寿命长的特点。专利US5225572制...
【技术保护点】
一种溶胶法制备的均苯四酸二酐的多组分低钒催化剂，其特征在于，包括主催化剂和助催化剂，所述主催化剂为V2O5和TiO2，V：Ti摩尔比为1：0.1～1：5；助催化剂为B2O3、SnO2和CeO2，以V的物质的量基准为1，则B的物质的量为0.001‑0.1，Sn的物质的量为0.001‑0.1，Ce的物质的量为0.001‑0.1。
【技术特征摘要】
1.一种溶胶法制备的均苯四酸二酐的多组分低钒催化剂，其特征在于，包括主催化剂和助催化剂，所述主催化剂为V2O5和TiO2，V：Ti摩尔比为1：0.1～1：5；助催化剂为B2O3、SnO2和CeO2，以V的物质的量基准为1，则B的物质的量为0.001-0.1，Sn的物质的量为0.001-0.1，Ce的物质的量为0.001-0.1。2.根据权利要求...
【专利技术属性】