The present invention provides a method for acrylic modified walnut shell of adsorbent and its preparation method, which comprises the following steps: (1) the walnut shell of washing, crushing and sieving, select 60~80 to walnut shell particles; (2) soaking step Potassium Permanganate solution (1) the walnut shell particles so that it is in the lead state; (3) the step (2) of the walnut shell happened acrylic modified walnut shell of chemical grafting reaction with acrylic acid and hexane heating; (4) the step (3) of the modified walnut shell with ethyl acetate and washed with deionised water to a certain temperature, drying after collection acrylic products, walnut shell of adsorbent obtained. The adsorbent obtained by the invention is suitable for the adsorption of metal ions in various kinds of sewage, especially the harmful heavy metal ions.
【技术实现步骤摘要】
一种丙烯酸改性的核桃壳吸附剂及其制备方法
本专利技术涉及一种酸改性的核桃壳吸附剂的制备方法，特别是一种用于吸附金属离子的丙烯酸改性的核桃壳吸附剂的制备方法。
技术介绍
在我国，水资源严重短缺，并且伴随着工业的快速发展和人口的极具增长，大量工业废水和生活废水未经处理就被排放到环境中，会对水体造成严重污染，尤其是重金属和水体富营养化，它们对水体造成最为严重的污染。对于重金属污染，不但不会被生物降解，而且还可以通过食物链在动植物体中存留、富集和迁移，一旦进入人体，将对人体产生长期而不可逆转的影响。因此，对水体中重金属污染的治理刻不容缓。常见的去除水体中金属污染物的方法有化学沉淀法、离子交换法、溶剂萃取法、电渗析法、反渗透法、超滤法等，其中，吸附及离子交换法因其效果好、成本低、操作方便等特点被广泛应用于金属离子工业废水的处理中。核桃壳结构性质如孔隙率、比表面积都较高；功能性基团性质如含有较多的羟基、羧基等，都为核桃壳吸附重金属离子提供了大量的活性位点，因此，核桃壳可以直接作为吸附剂使用。目前，用于吸附、分离金属离子的有关核桃壳吸附剂的绝大多数改性工艺都是以生成活性炭为最终...
【技术保护点】
一种丙烯酸改性的核桃壳吸附剂及其制备方法，其特征在于包括以下步骤：（1）称取适量的核桃壳，用清水洗涤，过滤后在90 ℃下干燥至恒重，粉碎筛分，收集60 ~80目的颗粒，并将颗粒用去离子水浸泡24 h，过滤后在90 ℃下干燥至恒重，备用；（2）称取适量的步骤（1）所得核桃壳颗粒，在30 ℃下用浓度为12.0~18.0 mmol•L
【技术特征摘要】
1.一种丙烯酸改性的核桃壳吸附剂及其制备方法，其特征在于包括以下步骤：（1）称取适量的核桃壳，用清水洗涤，过滤后在90℃下干燥至恒重，粉碎筛分，收集60~80目的颗粒，并将颗粒用去离子水浸泡24h，过滤后在90℃下干燥至恒重，备用；（2）称取适量的步骤（1）所得核桃壳颗粒，在30℃下用浓度为12.0~18.0mmol•L-1高锰酸钾溶液浸泡一定时间后，过滤并用去离子水洗涤，洗涤至上清夜为无色；（3）将步骤（2）所得核桃壳和适量的丙烯酸以及正己烷加入到三口烧瓶中，在搅拌下加热回流1~2h，再加入适量乙酸乙酯继续搅拌...
【专利技术属性】
技术研发人员：曾作祥，励沈劢尚，程利萍，薛为岚，方鹏，周佳宇，
申请(专利权)人：华东理工大学，
类型：发明
国别省市：上海,31