一种硝酸盐处理剂的制备及应用制造技术
Preparation and application of a nitrate treatment agent
The invention discloses a nitrate treatment agent preparation and application, the invention of cotton as template, using zinc iron titanium three hydrotalcite with biological morphology were synthesized by the coprecipitation method, after roasting in muffle furnace, nitrate salt treatment agent. The invention also provides the application of the nitrate treatment agent prepared by the method in the treatment of nitrate wastewater. The nitrate treatment agent prepared by the method has good adsorption effect on nitrate and is easy to separate. The regeneration method is simple and feasible, and has broad application prospects in the field of nitrate wastewater treatment.
【技术实现步骤摘要】
一种硝酸盐处理剂的制备及应用
本专利技术属于废水处理
，尤其涉及一种硝酸盐处理剂的制备及应用。
技术介绍
随着工农业的不断发展，农业化肥的大量使用、生活污水的排放以及工业废水的渗漏等问题，使得水中的硝酸盐污染越来越严重。过量的硝酸盐使水体中营养物质增多，促使自养型生物旺盛生长，造成水质恶化，破坏生态环境。硝酸盐化学稳定性强，不易与其他化合物结合，但其可在人体内转化成亚硝酸盐，此外，在各种含氮有机化合物的作用下，硝酸盐和亚硝酸盐会形成“三致”物质，可引发癌症、克山病和高铁血红蛋白症等疾病。因此，去除水体中硝酸盐刻不容缓。目前针对水体中硝酸盐的去除主要有生物法、反渗透法、离子交换法、金属催化还原法等，其中，生物反硝化法反应慢，需要有机物作为电子供体，会带来二次污染；反渗透法运行费用过高,而且不具有选择性,去除硝酸盐的同时也可能去除其他对人体有益的元素；离子交换法产生的浓缩废水较难处理；催化还原法对硝酸盐的还原一般需要采用贵金属做催化剂，一方面提高了处成本，另一方面如果催化剂选择不恰当会产生亚硝酸盐和氨氮等副产物。层状双金属氢氧化物(LDH)，又称类水滑石(HTl...
【技术保护点】
一种硝酸盐处理剂的制备方法，其特征在于以棉花为模板，采用共沉淀法合成具有生物形态的锌钛铁三元类水滑石，经过马弗炉焙烧，得到硝酸盐处理剂，具体步骤如下：(1)将棉花用蒸馏水和无水乙醇洗涤三次，60℃烘干备用；(2)将硝酸锌、硫酸钛和硝酸铁按照锌、钛、铁摩尔比1～3:1～3:1～3的比例制得混合盐溶液A，混合液总金属离子浓度控制为0.3～1mol/L；(3)配置共沉淀剂溶液B，溶液B中含1～5mol/L NaOH和0.1～0.5mol/L Na2CO3，溶液B体积是溶液A体积的1～2倍；(4)将处理过的棉花放入烧杯中，同时加入溶液A+溶液B体积的蒸馏水，棉花与蒸馏水的质量比是1...
【技术特征摘要】
1.一种硝酸盐处理剂的制备方法，其特征在于以棉花为模板，采用共沉淀法合成具有生物形态的锌钛铁三元类水滑石，经过马弗炉焙烧，得到硝酸盐处理剂，具体步骤如下：(1)将棉花用蒸馏水和无水乙醇洗涤三次，60℃烘干备用；(2)将硝酸锌、硫酸钛和硝酸铁按照锌、钛、铁摩尔比1～3:1～3:1～3的比例制得混合盐溶液A，混合液总金属离子浓度控制为0.3～1mol/L；(3)配置共沉淀剂溶液B，溶液B中含1～5mol/LNaOH和0.1～0.5mol/LNa2CO3，溶液B体积是溶液A体积的1～2倍；(4)将处理过的棉花放入烧杯中，同时加入溶液A+溶液B体积的蒸馏水，棉花与蒸馏水的质量比是1：60～1：250，然后将混合盐溶液A与共沉淀剂溶液B同时滴加于其中，控制滴加速度为每秒1滴，同时磁力剧烈搅拌，滴加完毕后，继续搅拌30min，超声10min，调节pH为9.5～10.5，得到悬浮液C；(5)将...