The invention discloses a preparation method of ethyl cellulose with ionic liquid gas separation membrane, which is characterized in that the ethyl cellulose (0.5g), ethanol (0.011mol, 12.65ml) is completely dissolved in solution, then add 1 allyl 3 tetrafluoroborate (0.002mol, 0.5g), under the temperature of 25 DEG C, stirring the reaction of 24 hours, the reaction solution is uniformly dispersed in a clean glass plate, at 25 DEG C, the solvent was ethyl cellulose and 1 allyl 3 tetrafluoroborate gas separation membrane, testing of products. The invention of the separation of the mixed gas in the N2/CO2, there are the separation of very high performance and through the performance.
【技术实现步骤摘要】
乙基纤维素与离子液体气体分离膜的制备方法
本专利技术属高分子材料与工程领域,特别涉及乙基纤维素与1-烯丙基-3-甲基咪唑四氟硼酸盐气体分离制备膜的制备方法。
技术介绍
气体分离膜作为分离温室气体的有效手段，它既经济有实用，而且绿色环保，符合低碳经济，符合可持续发展需要，将离子液体与高分子材料结合，得到的新型分离膜材料，成为当前离子液体研究领域的趋势之一，但离子液体与高分子材料间存在相容性很差易分层的问题，并且纯高分子分离膜气体选择性能低。
技术实现思路
本专利技术的目的在于提供乙基纤维素与1-烯丙基-3-甲基咪唑四氟硼酸盐共混膜的制备方法，解决了其相容性差和气体分离选择性低的问题，本专利技术专利采用的技术方案是：将乙基纤维素(0.5g)，在乙醇(0.011mol,12.65ml)溶液中完全溶解，再加入1-烯丙基-3甲基咪唑四氟硼酸盐(0.002mol,0.5g)，在25℃下,搅拌反应24个小时，将反应溶液均匀分散在干净的玻璃板上，在25℃下溶剂挥发,制得乙基纤维素和1-烯丙基-3-甲基咪唑四氟硼酸盐气体分离膜。本专利技术的有益效果是提供乙基纤维素与1-烯丙基-3甲基咪唑四氟硼酸盐气体分离膜的制备方法，制备了选择性,透过性高的气体分离膜。乙基纤维素与1-烯丙基-3-甲基咪唑四氟硼酸制备的气体分离膜的柔韧性增强,强度高，气体分离性能也有很大提高，N2的透过量达20.9Barrer较纯乙基纤维素膜相比增加10倍，CO2的透过量达810.9Barrer较纯乙基纤维素膜相比增加20倍，该膜分离系数平均值39，较纯乙基纤维素膜提高一倍。
【技术保护点】
乙基纤维素与离子液体气体分离膜的制备方法，其特征在于，将乙基纤维素(0.5g)，在乙醇(0.011mol, 12.65ml)溶液中完全溶解，再加入1‑烯丙基‑3甲基咪唑四氟硼酸盐(0.002mol, 0.5g)，在25℃下,搅拌反应24个小时，将反应溶液均匀分散在干净的玻璃板上，在25℃下溶剂挥发,制得乙基纤维素和1‑烯丙基‑3‑甲基咪唑四氟硼酸盐气体分离膜。
【技术特征摘要】
1.乙基纤维素与离子液体气体分离膜的制备方法，其特征在于，将乙基纤维素(0.5g)，在乙醇(0.011mol,12.65ml)溶液中完全溶解，再加入1-烯丙基-3甲基咪唑四氟硼酸盐...
【专利技术属性】
技术研发人员：贾宏葛，张辉，徐双平，藏雨，王建军，朱广宇，徐晨曦，王庆宇，
申请(专利权)人：齐齐哈尔大学，
类型：发明
国别省市：黑龙江,23