The invention relates to a crystalline silicon solar battery positive silver paste, a crystal silicon solar cell with positive silver paste, the positive silver paste including silver powder, lead-free glass powder, thixotropic agent and organic carrier, the lead-free positive silver paste also contains additives composition between the lead-free glass powder and additive weight the ratio of 1 to 0.1 5. The invention reduces the corrosion of the alkaline material in the lead-free glass powder to the EVA glue film of the encapsulation material of the battery, avoids the protective effect of the EVA material on the packaging material because of delamination, and improves the service life of the battery.
【技术实现步骤摘要】
一种晶体硅太阳能电池无铅正银浆料
本专利技术涉及一种晶体硅太阳能电池无铅正银浆料，属于太阳能电池
技术介绍
太阳能是一种绿色能源，因其无污染、取之不竭、不受地域资源限制等优点而越来越受到人们的重视，所以太阳能电池应运而生。晶硅太阳能电池是一种能够对光能响应并能将光能转换成电能的器件，它可以利用光生伏特效应将光能转换为电能。当阳光照射到电池板时，在电池两极表面产生一定的电势差，接通外接电路，就可以产生电流。把若干个电池通过串联或并联的方式连接起来，再经过封装材料EVA胶膜(乙烯醋酸乙烯共聚物)密封保护，就能制成电池组件，进而组成电池方阵，与其他电子器件配合组成独立系统或并入电网，提供清洁的电力供应。晶硅太阳能电池电极包括正面银电极、背面银电极和铝背场电极，正面银电极是使用正面银浆经过丝网印刷、干燥、高温烧结形成，正面银浆的性能直接决定了太阳能电池片正面银电极的性能，是晶体硅太阳能电池制造中的关键材料。目前，晶硅太阳能电池用正银浆料通常由银粉、无铅玻璃粉和有机载体制备而成，大多数正银浆使用含有较高比例氧化铅的玻璃粉。为了更好地维护人类赖以生存的生活环境，电子...
【技术保护点】
一种晶体硅太阳能电池无铅正银浆料，其特征在于：所述正银浆料的原料组分及重量含量如下：银粉87‑92份、有机载体5‑10份、无铅玻璃粉1～5份和触变剂0.1～3份，其中各组分的重量百分数之和为100％。
【技术特征摘要】
1.一种晶体硅太阳能电池无铅正银浆料，其特征在于：所述正银浆料的原料组分及重量含量如下：银粉87-92份、有机载体5-10份、无铅玻璃粉1～5份和触变剂0.1～3份，其中各组分的重量百分数之和为100％。2.根据权利1所述的一种晶体硅太阳能电池无铅正银浆料，其特征在于：所述银份为高振实密度银粉，振实密度大于6g每立方厘米。3.根据权利1所述的一种晶体硅太阳能电池无铅正银浆料，其特征在于：所述无铅玻璃粉的组成和重量百分数为：Bi2O340-60％...
【专利技术属性】
技术研发人员：郭宏彬，
申请(专利权)人：江苏正能电子科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。