The invention provides an inorganic sulfur reducing agent to prepare the anti UV method of wool fabric, the method comprises the following steps: (1) the solution preparation: the inorganic sulfur reducing agent, urea and twelve sodium dodecyl sulfate dissolved into the water, then add the Zinc Oxide ofnanoparticles, under a vigorous agitation the solution of Zinc Oxide nanoparticles dispersed; (2) the wool fabric is in step (1) solution obtained in multiple padding; (3) the padding wool fabric after irradiation in infrared light; (4) irradiated wool fabric impregnated with polyethylene glycol solution during solidification, then washed with water and drying. The preparation technology is simple and cheap, and has little damage to wool fabrics, and does not change the surface properties of wool fabrics. Zinc Oxide nanoparticles have good fastness on wool fabrics. No binder is used in the preparation process, which is harmless and harmless.
【技术实现步骤摘要】
用无机含硫还原剂制备抗紫外羊毛织物
本专利技术涉及一种功能织物的制备方法，尤其是一种使用无机含硫还原剂制备抗紫外羊毛织物的方法。
技术介绍
将纳米粒子引入纺织纤维中，可以制备得到功能性纤维材料。目前将纳米粒子引入羊毛纤维的制备方法很多，如：吸附法，溶胶凝胶法，层层组装法，涂层法等。然而，吸附法通过主要通过分子间范德华力和离子键力使纳米粒子吸附到羊毛纤维表面，水洗牢度较低；溶胶凝胶法和层层组装法的工艺过程较长，且较难控制；涂层法是利用粘合剂将纳米粒子粘合到羊毛纤维表面，降低了羊毛纤维对人体的亲肤性。羊毛角蛋白是一种富含胱氨酸的蛋白质，胱氨酸中的二硫键是分子间相互交联，构成稳定的网状结构，是羊毛蛋白不溶于水的本质原因。无机含硫还原剂可以将二硫键还原成巯基，已经广泛用于羊毛角蛋白的溶解。
技术实现思路
本专利技术所要解决的技术问题是，针对以上现有技术存在的缺点，提出一种使用无机含硫还原剂制备抗紫外羊毛织物的方法。该制备技术简单易行，成本低廉，对羊毛织物的强力损伤小，不改变羊毛纤维表面性能，氧化锌纳米粒子在羊毛织物上具有良好的牢度；该制备过程中未使用任何粘合剂，无毒无害。为了...
【技术保护点】
一种使用无机含硫还原剂制备抗紫外羊毛织物的方法，其特征在于，包括如下步骤：（1）溶解液的制备：将无机含硫还原剂、尿素和十二烷基硫酸钠溶解到水中，然后加入氧化锌纳米粒子，剧烈搅拌下得到分散有氧化锌纳米粒子的溶解液；（2）将羊毛织物在步骤（1）所得的溶解液中多次浸轧；（3）将浸轧后的羊毛织物在红外线下辐照10‑30min；（4）将辐照后的羊毛织物浸渍于聚乙二醇溶液中凝固，然后水洗、烘干。
【技术特征摘要】
1.一种使用无机含硫还原剂制备抗紫外羊毛织物的方法，其特征在于，包括如下步骤：（1）溶解液的制备：将无机含硫还原剂、尿素和十二烷基硫酸钠溶解到水中，然后加入氧化锌纳米粒子，剧烈搅拌下得到分散有氧化锌纳米粒子的溶解液；（2）将羊毛织物在步骤（1）所得的溶解液中多次...