一种不易分解的导光板材料及其制备方法技术

本发明专利技术提供了一种不易分解的导光板材料，该导光板材料包括：PMMA、PC、光扩散剂、光稳定剂、热稳定剂、相容剂、增韧剂。各组分的重量份数为：PMMA35‑60、PC25‑40、光扩散剂1‑8、光稳定剂0.3‑3、热稳定剂15‑20、相容剂0.1‑3、增韧剂2。本发明专利技术的配方加入光稳定剂可以吸收紫外线，加入热稳定剂可以使导光板具有良好的热稳定性，均可以有效地阻止导光板材料的分解。

An undecomposable material for light guide plate and its preparation method

The invention provides a material for light guide plate which is not easy to be decomposed. The light guide plate material includes PMMA, PC, light diffuser, light stabilizer, heat stabilizer, compatibilizer and toughening agent. The weight of each component is: PMMA35 60, PC25 40, light diffusing agent 1 8, 3, 0.3 light stabilizer 15 heat stabilizer 20, 3, 0.1 compatibilizer toughening agent 2. The formulation of the invention can absorb ultraviolet light by adding light stabilizer, and adding heat stabilizer can make the light guide plate have good thermal stability, which can effectively prevent the decomposition of the light guide plate material.

【技术实现步骤摘要】
一种不易分解的导光板材料及其制备方法
本专利技术涉及一种不易分解的导光板材料技术背景导光板设计原理源于笔记本电脑的液晶显示屏，是将线光源转变为面光源的高科技产品。光学级亚克力(PMMA)/PC为基材，运用LCD显示屏及笔记本电脑的背光模组技术，透过导光点的高光线传导率，经电脑对导光点计算，使导光板光线折射成面光源均光状态制造成型。产品采用光谱分析原理与数码UV印刷技术相结合并在恒温、恒湿、无尘的环境条件下制作而成。具有超薄、超亮、导光均匀、节能、环保、无暗区、耐用、不易黄化、安装维修简单快捷等鲜明特点。目前市场上，几乎所有的手机、平板电脑、笔记本电脑等诸多智能终端都是以导光板作为背光源来配合显示屏工作，导光板的应用已经渗透到人类的生活中，在各种环境中都有其应用。虽然导光板的光学性能良好，但是其他的物理性能相对一些特殊环境(如高温、太空的射线环境)来说还是较弱，所以研发出一种能够用于特殊环境的导光材料有举足轻重的意义。
技术实现思路
针对上述现有技术存在的不足，本专利技术要解决的问题是提供一种不易分解的导光板材料。为解决上述问题，本专利技术对导光板材料的配方做了进一步的优化：在现有技术本文档来自技高网...

【技术保护点】
一种不易分解的导光板材料，由重量份数为PMMA35‑60、PC25‑40、光扩散剂1‑8、光稳定剂0.3‑3、热稳定剂15‑20、相容剂0.1‑3、增韧剂2‑5混合而成。

【技术特征摘要】
1.一种不易分解的导光板材料，由重量份数为PMMA35-60、PC25-40、光扩散剂1-8、光稳定剂0.3-3、热稳定剂15-20、相容剂0.1-3、增韧剂2-5混合而成。2.根据权利要求1所述的一种不易分解的导光板材料，其特征在于：所述光稳定剂为水杨酸苯酯。3.根据权利要求2所述的一种不易分解的导光板材料，其特征在于：所述热稳定剂为玻璃纤维或蒙脱土的...

【专利技术属性】
技术研发人员：廖勇军，陈明波，张诺寒，陈伟豪，张坤，
申请(专利权)人：广东谷麦光电科技股份有限公司，
类型：发明
国别省市：广东,44