The invention discloses a plastic surface processing method, which comprises the following steps: first, the plastic products were annealed, the annealing time of 1.5 3 hours, 50 annealing temperature of 70 DEG C; the use of gasoline or alcohol cleaning plastic products, dryer drying, drying time of 0.5 1 small, drying temperature of 28 45 DEG C; and then use the spray gun to spray the surface of plastic products, plastic products and finally drying to spraying, drying time of 0.5 1 hours, 50 drying temperature 60 DEG C. The invention has simple process and convenient operation, and can cover the surface defects of the finished parts. The coating enhances the hardness and abrasion resistance of the plastic, and improves the corrosion resistance of the plastic.
【技术实现步骤摘要】
一种塑料制品表面加工方法
本专利技术具体涉及一种塑料制品表面加工方法。
技术介绍
塑料制品是采用塑料为主要原料加工而成的生活用品、工业用品的统称，现有技术中，对塑料制品所采用的喷涂效果不佳，从而影响塑料制品在使用中的抗腐蚀能力。
技术实现思路
针对上述问题，本专利技术提出一种塑料制品表面加工方法。一种塑料制品表面加工方法，包括以下步骤：先对塑料制品进行退火处理，退火时间1.5-3小时，退火温度50-70℃；再对塑料制品用汽油或酒精清洗，烘干器烘干，烘干时间0.5-1小时，烘干温度28-45℃；然后利用喷枪对着塑料制品的表面进行喷涂，最后对喷涂的塑料制品进行烘干，烘干时间0.5-1小时，烘干温度50-60℃。本专利技术的有益效果：本专利技术过程简单，操作方便，且可遮盖成型后制件的表面缺陷，涂层增强了塑料的硬度和耐擦伤性；提高了塑料的耐腐蚀性。具体实施方式一种塑料制品表面加工方法，包括以下步骤：先对塑料制品进行退火处理，退火时间1.5-3小时，退火温度50-70℃；再对塑料制品用汽油或酒精清洗，烘干器烘干，烘干时间0.5-1小时，烘干温度28-45℃；然后利用喷枪对着塑料...
【技术保护点】
一种塑料制品表面加工方法，其特征在于：包括以下步骤：先对塑料制品进行退火处理，退火时间1.5‑3小时，退火温度50‑70℃；再对塑料制品用汽油或酒精清洗，烘干器烘干，烘干时间0.5‑1小时，烘干温度28‑45℃；然后利用喷枪对着塑料制品的表面进行喷涂，最后对喷涂的塑料制品进行烘干，烘干时间0.5‑1小时，烘干温度50‑60℃。
【技术特征摘要】
1.一种塑料制品表面加工方法，其特征在于：包括以下步骤：先对塑料制品进行退火处理，退火时间1.5-3小时，退火温度50-70℃；再对塑料制品用汽油或酒精清洗，烘干器烘...