一种合成高纯度Ti3B2N的方法技术
A method for the synthesis of high purity Ti3B2N
The invention belongs to the field of structural materials, in particular a method for the synthesis of high purity Ti3B2N. According to the TiH2 powder, amorphous B powder, three kinds of raw materials six BN powder mole ratio of TiH2:B:BN=3: (0.9~1.1): (0.9~1.1), weigh TiH2 amorphous powder, B powder and six BN powder; will weigh TiH2 amorphous powder, B powder, BN six powder hunyun tablet, then in argon atmosphere at 10 DEG C 5~ /min the rate of heating to 1200~1300 Deg. C, thermal insulation 3~6h; after sintering, in an inert atmosphere, natural cooling to room temperature, high pure Ti3B2N. The invention has the following advantages: 1, the process is simple, and no hot pressing is required; 2, the process equipment is simple and the maintenance is convenient; 3, the purity of the Ti3B2N material prepared by the invention is as high as 75%.
【技术实现步骤摘要】
一种合成高纯度Ti3B2N的方法
本专利技术属于结构材料领域，尤其涉及一种合成高纯度Ti3B2N的方法。
技术介绍
Ti3B2N是一种新型的三元层状化合物，它具有高模量（杨氏模量430.22GPa，剪切模量181.06GPa），高强度等。同时，Ti3B2N具有很低的密度（理论密度4.80g/cm3）。作为一种最新发现的晶体具有较好的硬度和导电性，但其制备方法并不完善，申请人在早前申请的专利（申请号2016100610872）中，以Ti粉作为Ti源合成Ti3B2N的方法，产品纯度并不高，杂质TiN、TiB2含量较高。因此，制备高纯度Ti3B2N在研究高硬度、导电陶瓷材料领域具有很好的现实意义。
技术实现思路
为解决新型材料Ti3B2N合成纯度低的问题，本专利技术的目的在于提供一种合成高纯度Ti3B2N的方法，该方法工艺简单，适合工业规模化生产。为实现上述目的，本专利技术采取的技术方案如下：一种合成高纯度Ti3B2N的方法：按TiH2（氢化钛）粉、无定型B（硼）粉、六方BN（氮化硼）粉三种原料的摩尔比TiH2：B：BN=3：(0.9~1.1)：(0.9~1.1)，称取Ti...
【技术保护点】
一种合成高纯度Ti3B2N的方法，其特征在于：按TiH2粉、无定型B粉、六方BN粉三种原料的摩尔比TiH2：B：BN=3：(0.9~1.1)：(0.9~1.1)，称取TiH2粉、无定型B粉和六方BN粉；将称取的TiH2粉、无定型B粉、六方BN粉混匀，压片，然后在惰性保护气氛下以5~10℃/min的速率升温至1200~1300℃，保温3~6h；烧结完成后，在惰性保护气氛下，自然冷却至室温，得高纯Ti3B2N。
【技术特征摘要】
1.一种合成高纯度Ti3B2N的方法，其特征在于：按TiH2粉、无定型B粉、六方BN粉三种原料的摩尔比TiH2：B：BN=3：(0.9~1.1)：(0.9~1.1)，称取TiH2粉、无定型B粉和六方BN粉；将称取的TiH2粉、无定型B粉、六方BN粉混匀，压片，然后在惰性保护气氛下以5~10℃/min的速率升温至1200~1300℃，保温3~6h；烧结完成后，在...
【专利技术属性】
技术研发人员：胡前库，陈进峰，吴庆华，周爱国，王李波，
申请(专利权)人：河南理工大学，
类型：发明
国别省市：河南,41