The present invention relates to a biological carbon and its preparation method as well as the lead in water removal method, which comprises the following steps: 1) the washing drying, crushing, Caragana, extrusion molding, Section 2) by Caragana; in the atmosphere, the period of temperature programmed pyrolysis, Caragana, cooling, crude the crude product products; crushing, sieving, bio carbon; the pyrolysis temperature is 550 DEG C 680. The present invention in preparation of bio carbon sources of raw materials of Caragana wide and low cost, so that the waste, saving the cost of production, the preparation method is simple; the invention of Caragana raw materials rich in cellulose, cellulose and lignin, biochar prepared on the adsorption capacity of lead in water, the removal rate of 89.42 99.87% of lead, and the invention of biochar to facilitate the recovery, will not have two pollution.
【技术实现步骤摘要】
生物炭及其制备方法以及其对水体中铅的去除方法
本专利技术涉及一种生物炭，特别是涉及一种生物炭及其制备方法以及其对水体中铅的去除方法。
技术介绍
铅是目前最常见的对人体和植物危害最大的重金属元素之一。铅在土壤中的溶解度小，滞留时间长，是一种不可降解的环境污染物，在表土积累后，不仅影响农作物的产量和质量，而且在一些微生物的作用下转化成为毒性更强的化合物，通过食物链进入人体，影响人类健康。铅在进入人体后，主要贮存在骨骼中，少量分布在肾脏、神经及肌肉组织中，急性铅中毒会引起头痛、眩晕、贫血、困倦无力、肢体酸痛和腹绞痛等症状，慢性铅中毒则会引起人体神经衰弱等症状。此外，铅在植物组织内累积会影响植物进行呼吸作用和光合作用以及脂肪代谢等生理过程，过量的铅还会导致植物对水分的吸收大幅下降，影响植物的新陈代谢活动甚至导致死亡。近年来，随着国民经济的发展和人们生活水平的提高，由重金属铅导致的水污染问题越来越受到大众的关注。其中，重金属铅水污染的主要来源是采矿和冶炼行业。目前，吸附法是去除环境中重金属铅的主要方法。现有技术提出一种用于吸附污染水体中铅离子的吸附材料，该吸附材料是以环氧氯...
【技术保护点】
一种生物炭的制备方法，其特征在于：其包括以下步骤：1)将柠条洗涤，烘干，粉碎，挤压成型，得到柠条段；2)在气氛保护条件下，将所述的柠条段程序升温，热解，降温，得到粗产品；将所述的粗产品粉碎，过筛，得到生物炭；其中，热解温度为550‑680℃。
【技术特征摘要】
1.一种生物炭的制备方法，其特征在于：其包括以下步骤：1)将柠条洗涤，烘干，粉碎，挤压成型，得到柠条段；2)在气氛保护条件下，将所述的柠条段程序升温，热解，降温，得到粗产品；将所述的粗产品粉碎，过筛，得到生物炭；其中，热解温度为550-680℃。2.根据权利要求1所述的生物炭的制备方法，其特征在于，所述的柠条段的长度为1-4cm。3.根据权利要求1所述的生物炭的制备方法，其特征在于，所述的程序升温的速率为8-11℃/min。4.根据权利要求1所述的生物炭的制备方法，其特征在于，所述的热解温度为640-650℃。5.根据权利要求1所述的生物炭的制备方法，其特征在于，步骤2)中对所述的柠条段热解的时间为1-3h。6.根据权利要...
【专利技术属性】
技术研发人员：郑纪勇，王彤彤，周晓燕，张兴昌，
申请(专利权)人：西北农林科技大学，
类型：发明
国别省市：陕西,61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。