The invention discloses a three-dimensional silicon carbon soil conditioner, which is made up of weight percentage components: sodium zeolite powder 25 to 35%, calcium type zeolite 25 to 35%, medical stone 10 to 15%, diatomite 10 to 15%, six ring stone 10 ~ 15%. After mixing the above material fully, it is fine grinding to 300 mesh and then calcined at high temperature of 400 C for 2 hours, and after cooling, the packaging is used. Because the soil conditioner is made of high quality natural mineral processing activated, belongs to the class of active carbon porous material itself is rich in a variety of trace elements, processed after activation with adsorption, exchange, catalysis, curing function, and exchange adsorption of various heavy metal ions, ammonia nitrogen, nitrite and sulfide obviously, the effect is good, can reduce the and the prevention of soil pollution, soil can maintain a steady state for a long time in the removal of heavy metal in soil after.
【技术实现步骤摘要】
三维硅碳素土壤调理剂
本专利技术涉及一种土壤质量调理剂,尤其涉及一种三维硅碳素土壤调理剂。
技术介绍
随着经济与社会的不断发展,人类活动、社会工业化进程的加快,世界范围内土壤污染、土壤退化问题日益突出。土壤污染,大多数来源工业污染、生活污染、化肥、农药等,污染物主要是镉、铅、汞、氟、氨氮、硫化物、砷化物、酚化物、有机磷放射物等。土壤退化表现为土壤肥力贫瘠化、盐碱化、重金属污染化等。土壤污染、土壤退化的问题日益严重,已经对生态环境造成极大的危害,同时并对人体也产生了毒害作用。土地大面积盐渍化和重金属超标已严重影响农作物生长,严重限制了土地生产力的发展,增加了农业生产成本,影响了农作物的产量和质量。针对土壤污染、土壤退化的治理问题,当前人们应用了一些土壤调理剂,对改善土壤污染、土壤退化起到了一定的作用,但由于调理剂中含有大量的化学成分,使用不当容易土壤造成二次污染,不利于推广应用。
技术实现思路
为了解决现有技术的不足,本专利技术的目的是提供一种由天然材料制成的三维硅碳素土壤调理剂。该调理剂对土壤中的大多数污染物有吸附作用和离子交换作用。实现本专利技术的目的采用的技术方案如下:该三维硅碳素土壤调理剂按重量百分比成分组成:钠型沸石粉25~35%,钙型沸石粉25~35%,麦饭石10~15%,硅藻土10~15%,六环石10~15%。将上述材料充分混合后,细磨到300目,然后再经过400℃的高温煅烧2小时,冷却后包装使用。本专利技术的有益效果是:由于土壤调理剂由优质天然矿物质加工活化组成,属于类活性炭多孔物质,本身富含多种微量元素,经加工活化后具有吸附、交换、催化、固化功 ...
【技术保护点】
一种三维硅碳素土壤调理剂,其特征在于:所述的三维硅碳素土壤调理剂按重量百分比成分组成:钠型沸石粉25~35%,钙型沸石粉25~35%,麦饭石10~15%,硅藻土10~15%,六环石10~15%,将上述材料充分混合后,细磨到300目,然后再经过400℃的高温煅烧2小时,冷却后包装使用。
【技术特征摘要】
1.一种三维硅碳素土壤调理剂,其特征在于:所述的三维硅碳素土壤调理剂按重量百分比成分组成:钠型沸石粉25~35%,钙型沸石粉25~35%,麦饭石...