A kind of high temperature resistant waterproof material, which comprises the following parts by weight of materials: 90# 30 heavy traffic asphalt 45, antioxidant 4010 4 10, APAO 10 modifier 20, styrene butadiene styrene block copolymer modifier 5 10, minus three line oil plasticizer 0.5 2 copies, 25 copies of 15 talcum powder. The invention provides a high temperature resistant waterproof material and its preparation process, using the SBS modifier and water, weak acid, alkali and other contact, with high tensile strength, surface friction coefficient, low temperature performance, good processing performance and other characteristics; the APAO modifier has strong weatherability, excellent salt resistance and SBS, elastomer, asphalt and other raw materials have good compatibility and other advantages, to SBS elastomer modified such as high and low temperature performance, weather resistance plays an important and significant role; the reduction of three line oil plasticizer also can improve the compatibility of asphalt and modifier.
【技术实现步骤摘要】
一种耐高温防水材料及其制备工艺
本专利技术属于防水材料领域，具体涉及一种耐高温防水材料及其制备工艺。
技术介绍
随着我国经济的快速发展，高速公路、道路和桥梁的建设数量有了较快增长。然而，诸多道路和桥梁通车不到一年便出现早期损坏，其中危害最大、最常见的就是水损害。为了延长道路和桥梁的使用寿命，减少维修费用，在道桥面上布设防水层是十分必要的。自20世纪80年代以来，SBS改性沥青防水材料作为国家重点推广的新型建筑防水材料，因具有价格适中、防水效果好、施工方便等优点，迅速在建筑防水行业得到了推广应用并迅猛发展。苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)改性沥青防水材料以其优异的低温及防水性能在道桥上得到了较广泛的应用，随着防水企业业务的拓展，但是在一些高温地区，由于环境条件的限制，传统SBS改性沥青防水材料已不能满足使用要求，需要研究开发一种耐高温防水材料。专利CN106085013A公开了一种耐高温防水材料及其制备方法，该防水材料能够满足高温环境下的防水作业需求。专利CN104177026A公开了一种耐高温防水材料，具有良好耐高温和低温温度变化，能和水泥、混凝土形成同...
【技术保护点】
一种耐高温防水材料，其特征在于，包括以下重量份材料：
【技术特征摘要】
1.一种耐高温防水材料，其特征在于，包括以下重量份材料：2.一种权利要求1所述的一种耐高温防水材料的制备工艺，其特征在于，步骤包括：1)按比例称取原料；2)将90#重交道路沥青在110-120℃条件下加热脱水后升温至180℃，加入减三线油增塑剂混合加热搅拌；3)保持温度为180℃，加入防老剂4010、APAO改性剂和苯乙烯-丁二烯-苯乙烯嵌段共聚物改性剂搅拌，搅拌速度为400r/min，搅拌时间为1...
【专利技术属性】
技术研发人员：乔启信，
申请(专利权)人：安徽朗凯奇建材有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。