The present invention relates to a new type of rock wool for blocking the curtain wall. Contains the following components, each component according to the weight ratio of 55: 70%, 9 basalt 14% magnetite ore, 6 8%, 10 slag 12% dolomite. The invention relates to a novel sealing curtain wall rock wool board, specifically, relates to an adding magnetite ore raw materials, and reduce the amount of binder spraying, to increase the content of iron in rock wool products, the fireproof performance is improved, the ratio of raw materials through several tests, adjusting the proportion of magnetite composite material, the final choose the best formula of the invention, and can guarantee the stable operation of cupola.
【技术实现步骤摘要】
一种幕墙封堵用新型岩棉
本专利技术涉及一种幕墙封堵用新型岩棉,属于防火材料
技术介绍
岩棉是以天然矿物岩石为原料,经过高温融熔加工成的人工无机纤维合成体。传统岩棉是以玄武岩为主要原料制成,具有土黄色外观。本专利技术提及的幕墙封堵用岩棉通过采用新的原料配比,加以辅料,并通过粘结剂喷施量的调整,使得其岩棉产品的耐火极限大提高,在实际应用中,整体提升了幕墙系统的耐火性能。
技术实现思路
本专利技术针对上述缺陷,目的在于提供一种提高防火封堵突出性能的一种幕墙封堵用新型岩棉。为此本专利技术采用的技术方案是:本专利技术包含有以下组分,55-70%的玄武岩、9-14%的磁铁矿石、6-8%的矿渣、10-12%的白云石。所述磁铁矿石为含铁量(重量比)为70-80%的铁矿石。还包括有1-2%的辅料铝矾土。所述磁铁矿石的含量为12-14%。所述玄武岩含量为55-60%。本专利技术的优点是:本专利技术利用原料配方的调整,在原料中添加铁矿石及少量的辅料,以及减少粘结剂的喷施量,达到提高防火封堵的突出性能。具体来说,本专利技术在原料中添加磁铁矿石,以及减少粘结剂喷施量,来增加岩棉产品中铁的含量,使得其产品耐火性能得到提升;通过多次原料配比试验,不断调节组合料中磁铁矿石的比例,最终选择本专利技术中的最优配方,且能保证冲天炉运行稳定。具体实施方式本专利技术原料中添加含铁量为70-80%的铁矿石,将55-60%的玄武岩、12-14%的磁铁矿石、6-8%的矿渣、10-12%的白云石及少量的辅料(1-2%的铝矾土),并加入适量焦炭为燃料组成混合料进入冲天炉熔融;由于磁铁矿石的加入,使得其 ...
【技术保护点】
一种幕墙封堵用新型岩棉,其特征在于,包含有以下组分,各组分按重量比为:55‑70% 的玄武岩、9‑14% 的磁铁矿石、6‑8%的矿渣、10‑12% 的白云石。
【技术特征摘要】
1.一种幕墙封堵用新型岩棉,其特征在于,包含有以下组分,各组分按重量比为:55-70%的玄武岩、9-14%的磁铁矿石、6-8%的矿渣、10-12%的白云石。2.根据权利要求1所述的一种幕墙封堵用新型岩棉,其特征在于,所述磁铁矿石为含铁量(重量比)为70-80%的铁矿石。3.根据权利要求1所述的一种幕墙封堵用新型岩棉...