一种胸肌支架防滑套制造技术
An antiskid sleeve of the chest muscle scaffold
The invention relates to a breast bracket antiskid sleeve, which comprises a rubber antiskid layer from top to bottom, PTFE fiber layer, layer, and memory cotton felt layer magnetic polymer material layer; the rubber antiskid fiber layer thickness is 2 3mm, the PTFE layer thickness is 0.5 1.5mm, the memory foam layer the thickness of 5 8mm, the felt layer thickness is 1 2mm, the magnetic polymer material layer thickness of 0.5 1.0mm. The anti-skid sleeve of the invention has good skid resistance and strong sweat absorption, and can connect with the chest bracket body through the polymer magnetic material layer, and the connection is stable and not easy to fall off.
【技术实现步骤摘要】
一种胸肌支架防滑套
本专利技术涉及健身器材领域，尤其涉及一种胸肌支架防滑套。
技术介绍
现有的防滑套多以发泡塑料制成，耐磨性及耐腐蚀性差，每隔一段时间就需要更换一次，且吸汗性能不好。
技术实现思路
为了解决上述技术问题，提供一种防滑、吸汗、耐用的防滑套，本专利技术提供以下技术方案：一种胸肌支架防滑套，自上而下依次包括橡胶防滑纤维层、聚四氟乙烯层、记忆棉层、毛毡层以及高分子磁性材料层；所述橡胶防滑纤维层厚度为2-3mm、所述聚四氟乙烯层的厚度为0.5-1.5mm、所述记忆棉层的厚度为5-8mm、所述毛毡层厚度为1-2mm、所述高分子磁性材料层的厚度为0.5-1.0mm。进一步的，所述橡胶防滑纤维层厚度为2.5mm、所述聚四氟乙烯层的厚度为1.0mm、所述记忆棉层的厚度为6.5mm、所述毛毡层厚度为1.5mm、所述高分子磁性材料层的厚度为0.75mm。进一步的，所述防滑套总厚度不超过12mm。本专利技术的有益效果在于：防滑性能好、吸汗性强，且通过高分子磁性材料层即可与胸肌支架本体进行连接，连接稳固且不易脱落。附图说明图1、本专利技术的层结构示意图。具体实施方式一种胸肌支架防滑套，自上而下依次包括橡胶防滑纤维层1、聚四氟乙烯层2、记忆棉层3、毛毡层4以及高分子磁性材料层5；所述橡胶防滑纤维层1厚度为2.5mm、所述聚四氟乙烯层2的厚度为1.0mm、所述记忆棉层3的厚度为6.5mm、所述毛毡层4厚度为1.5mm、所述高分子磁性材料层5的厚度为0.75mm。以上述依据本专利技术理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项专利技术技术思想的范围内...
【技术保护点】
一种胸肌支架防滑套，其特征在于：自上而下依次包括橡胶防滑纤维层、聚四氟乙烯层、记忆棉层、毛毡层以及高分子磁性材料层；所述橡胶防滑纤维层厚度为2‑3mm、所述聚四氟乙烯层的厚度为0.5‑1.5mm、所述记忆棉层的厚度为5‑8mm、所述毛毡层厚度为1‑2mm、所述高分子磁性材料层的厚度为0.5‑1.0mm。
【技术特征摘要】
1.一种胸肌支架防滑套，其特征在于：自上而下依次包括橡胶防滑纤维层、聚四氟乙烯层、记忆棉层、毛毡层以及高分子磁性材料层；所述橡胶防滑纤维层厚度为2-3mm、所述聚四氟乙烯层的厚度为0.5-1.5mm、所述记忆棉层的厚度为5-8mm、所述毛毡层厚度为1-2mm、所述高分子磁性材料层的厚度为0.5-1.0mm。2...
【专利技术属性】
技术研发人员：张阳辉，
申请(专利权)人：丹阳市飞利健身器材有限公司，
类型：发明
国别省市：江苏,32