表面保护膜制造技术

本发明专利技术涉及表面保护膜。本发明专利技术提供一种适合于在具有聚酯类基材的同时一并实现良好的手撕性和高再加工性的表面保护膜。本发明专利技术的表面保护膜(X)具有包含作为透明基材的基材(11)和粘合剂层(12)的层叠结构。基材(11)是具有75μm以上的厚度的基材宽度方向单轴拉伸聚酯类基材。表面保护膜(X)的基材宽度方向上的埃尔门多夫撕裂强度为0.5N以下，且表面保护膜(X)的基材长度方向上的埃尔门多夫撕裂强度为1N以上。

Surface protective film

The present invention relates to a surface protection film. The present invention provides a surface protection film suitable for achieving good hand tearing and high reprocessing at the same time as a polyester base material. The surface protection film (X) of the present invention has a laminated structure containing a substrate (11) and an adhesive layer (12) as a transparent substrate. The base material (11) is a single axis tensile polyester base material with a thickness of more than 75 m. The Elmendorf tear strength of the surface protection film (X) in the width direction is less than 0.5N, and the tear strength of the surface protection film (X) in the length direction of the substrate is more than 1N.

【技术实现步骤摘要】
表面保护膜
本专利技术涉及具有透光性的表面保护膜。
技术介绍
近年来，在各种
中利用具有高透明性的表面保护膜。例如在平板显示器(FPD)的
中，对于组装于FPD的各种光学部件而言，出于在其制造过程、检查工序、运输过程等中的表面保护的目的，有时在部件表面贴合表面保护膜。这样的表面保护膜例如记载于下述专利文献1～3中。现有技术文献专利文献专利文献1：日本特开2012-17399号公报专利文献2：日本特开2015-157964号公报专利文献3：日本特开2016-74899号公报
技术实现思路
专利技术所要解决的问题作为表面保护膜的基材而言，有时采用聚酯类基材，因为其耐热性、透明性、尺寸稳定性等各种特性优异。对于作为用于光学部件用途的表面保护膜等的透光性的聚酯类基材的例如PET膜而言，已知多数情况下在制造工艺中通过T型模头法将原料树脂材料挤出成形为膜状、然后经过包含沿该膜的流动方向或长度方向(MD)的拉伸和沿宽度方向(TD)的拉伸的双轴拉伸处理。另外，对于表面保护膜而言，从作业效率等观点考虑，有时还要求良好的手撕性。本专利技术基于如上所述的情况而想出，其目的在于提供一种适合于在具有聚本文档来自技高网...

【技术保护点】
一种表面保护膜，其中，所述表面保护膜具有包含透明基材和粘合剂层的层叠结构，所述透明基材为基材宽度方向单轴拉伸聚酯类基材且具有75μm以上的厚度，并且所述表面保护膜在基材宽度方向上的埃尔门多夫撕裂强度为0.5N以下且在基材长度方向上的埃尔门多夫撕裂强度为1N以上。

【技术特征摘要】
2016.07.05 JP 2016-1330991.一种表面保护膜，其中，所述表面保护膜具有包含透明基材和粘合剂层的层叠结构，所述透明基材为基材宽度方向单轴拉伸聚酯类基材且具有75μm以上的厚度，并且所述表面保护膜在基材宽度方向上的埃尔门多夫撕裂强度为0.5N以下且在基材长度方向上的埃尔门多夫撕裂强度为1N以上。2.如权利要求1所述的表面保护膜，其中，所述透明基材的厚度为150μm以下。3.如权利要求1所述的表面保护膜，其中，所述透明基材的宽度方向的...

【专利技术属性】
技术研发人员：三井数马，野中崇弘，冲田奈津子，
申请(专利权)人：日东电工株式会社，
类型：发明
国别省市：日本,JP