The invention relates to the field of paint, in particular to a anti - ice coating for a fireproof valve and a preparation method. The invention is composed of the following parts by weight of the components of isophorone diisocyanate 34 66, 20 34 nano zinc sulfide and four phthalic anhydride chloride two 10 16 copies, 6 copies, 3 arsenic trioxide petroleum ether 16 20 copies, 10 copies of the 6 curing agent, catalyst 0.6 1.6 copies, 60 copies, 36 dilution agent isopropanol 10 calcium 16 vinyl chloride, 10 16 copies, 10 copies of 7 furan. The anti icing coating is designed to be insulated from the surface of the surface of the coating, and uses ice water as a switch on the surface of the insulator.
【技术实现步骤摘要】
一种防火阀的防冰涂料及其制备方法
本专利技术涉及涂料领域,尤其涉及一种防火阀的防冰涂料及其制备方法。
技术介绍
防火阀是一种藉易熔合金的温度控制,利用重力作用和弹簧机构的作用关闭的阀门形式。新型产品中亦有利用记忆合金产生形变使阀门关闭的。它的作用是:当烟气温度达到280℃时,人已基本疏散完毕,排烟已无实际意义,而烟气中此时已带火,阀门自动关闭,以避免火势蔓延。
技术实现思路
本专利技术的目的在于提供一种防火阀的防冰涂料及其制备方法,以解决上述技术问题。本专利技术为解决上述技术问题,采用以下技术方案来实现:一种防火阀的防冰涂料及其制备方法,是由以下重量份数的组分组成:异佛尔酮二异氰酸酯34-66份纳米硫化锌20-34份四氯邻苯二甲酸酐10-16份三氧化二砷3-6份石油醚16-20份熟化剂6-10份催化剂0.6-1.6份稀释剂36-60份异丙醇钙10-16份氯乙烯10-16份呋喃7-10份。一种防火阀的防冰涂料的制备方法,包括以下步骤:(1)将异佛尔酮二异氰酸酯、四氯邻苯二甲酸酐、三氧化二砷、石油醚、熟化剂和催化剂在反应釜中按上述比例充分混合反应,然后加入稀释剂、纳米硫化锌充分混合,最终制得混合液;(2)取上述比例的异丙醇钙、氯乙烯和呋喃,将异丙醇钙溶解在氯乙烯和呋喃混合液中,放入超声波清洗器中震荡34min,与步骤(1)中的混合液混合搅拌制成。本专利技术的有益效果:本专利技术防冰涂料通过设计绝缘于表曲涂料喷涂方式,利用绝缘子表面冰水充当开关。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本专利技术 ...
【技术保护点】
一种防火阀的防冰涂料,其特征在于,是由以下重量份数的组分组成。异佛尔酮二异氰酸酯34‑66份纳米硫化锌20‑34份四氯邻苯二甲酸酐10‑16份三氧化二砷3‑6份石油醚16‑20份熟化剂6‑10份催化剂0.6‑1.6份稀释剂36‑60份异丙醇钙10‑16份氯乙烯10‑16份呋喃7‑1O份。
【技术特征摘要】
1.一种防火阀的防冰涂料,其特征在于,是由以下重量份数的组分组成。异佛尔酮二异氰酸酯34-66份纳米硫化锌20-34份四氯邻苯二甲酸酐10-16份三氧化二砷3-6份石油醚16-20份熟化剂6-10份催化剂0.6-1.6份稀释剂36-60份异丙醇钙10-16份氯乙烯10-16份呋喃7-1O份。2.一种权利要求1所述防火阀的防冰涂料的制备方...