一种抗菌防霉消臭的纳米复合颗粒、其制备方法及应用技术
An antiseptic and deodorizing nano composite particle, its preparation and Application
The invention belongs to the technical field of the preparation of antibacterial materials, especially relates to an antibacterial nano composite particles, eliminating odor and its preparation method and application of the nano composite particles as aggregates of nanoparticles, the nano composite particle size is 10 500nm. Nano crystalline composite particles of the invention provides good nano composite particle size between 10 500nm, surface defect state nano composite particles have more, its simple preparation process, constant temperature heating curve using microwave muffle furnace, eliminating the long, fast particles agglomeration and surface flaw. Nano composite particles provided by the invention has strong anti-bacterial and deodorizing function, especially has obvious antibacterial activity against Staphylococcus aureus, Escherichia coli, Candida albicans, Penicillium etc..
【技术实现步骤摘要】
一种抗菌防霉消臭的纳米复合颗粒、其制备方法及应用
本专利技术属于抗菌材料制备
，尤其是涉及一种抗菌防霉消臭的纳米复合颗粒、其制备方法及应用。
技术介绍
众所周知，纳米氧化锌颗粒是一种具有抗菌活性的无机金属氧化物。作为紫外光催化剂，氧化锌通常是在紫外光激发下实现抗菌功能。然而在无光照的情况下氧化锌仍然可以表现出显著的抗菌性。最近研究表明，氧化锌抗菌活性主要源于表面氧空位缺陷。氧空位缺陷捕获电子后可以活化空气中的氧分子，产生具有强氧化性能力的活性氧物种。活性氧物种进而可以杀灭各种微生物，并且降解具有刺激性气味的可挥发性有机气体，从而具有除臭功能。这一研究揭示在氧化锌制备过程中对其表面缺陷结构进行调控是获得高抗菌活性的关键所在。氧化锌粉体的通常制备方法包括火法和湿法。火法(包括直接法和间接法)通常是由高温锌蒸汽和氧气反应制备氧化锌。水热法是湿法氧化锌的常规制备方法。这些方法通常可以得到结晶性能良好的氧化锌粉体材料，但是很难获得含有较多氧空位缺陷的氧化锌粉体材料。
技术实现思路
本专利技术的目的在于克服上述技术不足，提出一种抗菌防霉消臭的纳米复合颗粒。为达到上述技术目的...
【技术保护点】
一种抗菌防霉消臭的纳米复合颗粒，其特征在于，所述纳米复合颗粒为纳米颗粒的团聚体，所述纳米复合颗粒的粒径为10‑500nm。
【技术特征摘要】
1.一种抗菌防霉消臭的纳米复合颗粒，其特征在于，所述纳米复合颗粒为纳米颗粒的团聚体，所述纳米复合颗粒的粒径为10-500nm。2.根据权利要求1所述的抗菌防霉消臭的纳米复合颗粒，其特征在于，所述纳米复合颗粒为纳米氧化锌。3.根据权利要求1所述的抗菌防霉消臭的纳米复合颗粒，其特征在于，所述纳米复合颗粒的表面缺陷多。4.一种权利要求1所述的抗菌防霉消臭的纳米复合颗粒的制备方法，其特征在于，在空气气氛下，将有机盐置于微波马弗炉中，快速升温至高温，经高温热分解反应，冷却，即得。5.根据权利要求4所述的抗菌防霉消臭的纳米复合颗粒的制备方法，其特征在于，所述有机盐为有机锌盐。6.根据权...
【专利技术属性】
技术研发人员：陈兴军，王永峰，
申请(专利权)人：山东星美新材料股份有限公司，
类型：发明
国别省市：山东,37