一种掺铥碲锗酸盐中红外玻璃及其制备方法技术

本发明专利技术公开了一种掺铥碲锗酸盐中红外玻璃，其组分包括:TeO2,GeO2,ZnO,脱硝催化剂废料,Na2O,Tm2O3。通过熔融法制得的玻璃，中红外发光强度强，具有良好的热稳定性能，是一种非常有前景的高光学质量玻璃；利用废弃的脱硝催化剂废料增强玻璃的硬度和改善玻璃热稳定性性能，制备方法简便，制备周期短，有望应用于国防工业、军事及民用领域。

A kind of infrared glass in thulium tellurium germanate and its preparation method

The invention discloses a kind of infrared glass in thulium tellurium germanate salt, and its components include: TeO2, GeO2, ZnO, denitrification catalyst waste, Na2O, Tm2O3. Prepared by melting glass, mid infrared luminescence intensity, good thermal stability, is a kind of high quality optical glass is very promising; the use of waste and waste catalyst to enhance the performance of the thermal stability of glass and improve the hardness of glass, the preparation method is simple, short preparation period, is expected to be applied to national defense industrial, military and civil fields.

【技术实现步骤摘要】
一种掺铥碲锗酸盐中红外玻璃及其制备方法
本专利技术涉及一种掺铥碲锗酸盐中红外玻璃及其制备方法。
技术介绍
中红外2μm波段铥掺杂激光玻璃及光纤在国家安全与国防建设、天体物理探测与光谱学研究等领域都将具有广泛的应用前景。已有报道的2μm掺铥发光玻璃基本上都是基于Tm3+:3F4→3H6跃迁，获得中心波长在1.8μm的发光。目前，仅在氟化物玻璃、硅酸盐玻璃中获得2μm激光输出，氟化物玻璃因其固有的缺陷，化学稳定性和机械强度较差、制备条件苛刻、易被水分侵蚀、抗析晶性能差(ΔT≤85℃)等限制了其激光功率的提高。硅酸盐玻璃声子能量高(～1100cm～1)，稀土无辐射跃迁几率高，不利于获得高效发光。亟需发展一种声子能量低，热稳定性能优良的新型2μm波段掺铥玻璃体系。碲酸盐玻璃的声子能量较低(700～750cm～1)，有利于提高稀土辐射跃迁几率，发光效率较高。但是碲酸盐玻璃也存在热稳定性能、机械性能较差的问题，可通过在碲酸盐玻璃中添加适量GeO2替代一部分氧化碲作为玻璃形成体，形成碲锗酸盐玻璃，改善玻璃的热稳定性能和机械性能。但是二氧化锗引入后，玻璃折射率降低，不利于激光玻璃的增益性能。结合我国本文档来自技高网...

【技术保护点】
一种掺铥碲锗酸盐中红外玻璃，其特征在于，按质量百分比计，包括如下原料：

【技术特征摘要】
1.一种掺铥碲锗酸盐中红外玻璃，其特征在于，按质量百分比计，包括如下原料：2.如权利要求1所述的掺铥碲锗酸盐中红外玻璃的制备方法，其特征在于，该方法包括下列步骤：(1)原料预备：将脱硝催化剂废料在120～200℃进行煅烧55～65分钟，研磨后在325目过筛，筛余量小于5％；按照玻璃组成的质量百分比，计算出相应各组成的重量，称取原料；(2)制备技术：所有原料组分研磨均匀形成混合料后，放入黄金坩埚中，并置于750～800℃的硅碳棒电炉中熔...

【专利技术属性】
技术研发人员：徐时清，田颖，井绪峰，黄飞飞，张军杰，李兵朋，
申请(专利权)人：中国计量大学，
类型：发明
国别省市：浙江,33