A preparation method of oil soluble graphene quantum dots
The invention provides a preparation method of the oil soluble graphene quantum dots, which belongs to the technical field of nanomaterials preparation. The method comprises the following steps: (1) the citric acid is placed in the container to 180 250 DEG C melting, until the citric acid is orange; (2) adding oil amine in citric acid pyrolysis liquid orange, in 180 250 DEG C 3 8min; (3) the above will stop heating. The reaction by the dropwise addition of toluene, severe concussion, until completely mixing; (4) in the mixed solution of toluene with water, slow shake, static, until the solution is layered; (5) taking the toluene layer after freeze drying of solid powder obtained is oil soluble graphene amount sub point. The purity of the oil soluble graphene quantum dots prepared by the invention is high; the reagents used in the invention are common and easy to obtain, and the method is simple and easy to be prepared on a large scale.
【技术实现步骤摘要】
一种油溶性石墨烯量子点的制备方法
本专利技术涉及纳米材料的制备，具体属于一种油溶性石墨烯量子点的制备方法。
技术介绍
石墨烯量子点是尺寸小于10nm的石墨烯薄片。石墨烯量子点具有许多优异的性能，比如说较大的表面积，较高的机械性能，较高的电子迁移率，而且具有较好的生物相容性，因此在生物医学，电子材料，光学材料，磁性材料及环境检测等领域具有重要的应用前景。石墨烯量子点的制备方法主要分为两类，自上而下法和自下而上法。自上而下法是指将石墨烯片经过化学或物理处理，从而得到石墨烯量子点，具体包括电化学法，水热法，化学剥离碳纤维法等；自下而上法是指把一些小分子当做反应前体，经过一系列化学反应步骤而得到石墨烯量子点，具体包括化学气相沉积法，热解法，微波法等。目前油溶性石墨烯量子点一般为先合成量子点，然后再对其进行功能化修饰。但实现过程步骤繁琐，难以推广。CN201710381811公开了一种氮掺杂石墨烯量子点的熔融制备方法，在熔融条件下可以获得氮掺杂石墨烯量子点。但该方法制备的石墨烯量子点为水溶性，不是油溶性。而且该方法制备的量子点纯度难以得到保证。
技术实现思路
本专利技术的目的在...
【技术保护点】
一种油溶性石墨烯量子点的制备方法，其特征在于包括如下步骤：(1)取柠檬酸置于容器中于180‑250℃加热熔化，直到柠檬酸变为橙色；(2)在橙色的柠檬酸热解液中加入适量油胺，于180‑250℃反应3‑8min；(3)停止加热，将上述反应物逐滴加入甲苯中，剧烈震荡，直到完全混匀；(4)在上述混匀的甲苯溶液中加入水，缓慢摇匀，静置，直到溶液分层；(5)取上层甲苯层，经冷冻干燥，得到的固体粉末即为油溶性石墨烯量子点。
【技术特征摘要】
1.一种油溶性石墨烯量子点的制备方法，其特征在于包括如下步骤：(1)取柠檬酸置于容器中于180-250℃加热熔化，直到柠檬酸变为橙色；(2)在橙色的柠檬酸热解液中加入适量油胺，于180-250℃反应3-8min；(3)停止加热，将上述反应物逐滴加入甲苯中...
【专利技术属性】
技术研发人员：李忠平，朱瑞琦，杨振华，张月霞，李红荣，双少敏，董川，
申请(专利权)人：山西大学，
类型：发明