The invention relates to a silica modified method, which comprises the following steps: silica sand cleaning drying, and then preheated to 76 to 82 DEG C, a sand mixing machine, adding silica surface modification agent, mixed 50 ~ 70s, the modified silica sand; the invention relates to the modifier the wide source of raw materials, low cost, safe and non-toxic; the invention of the modifier method of silica modified simple, and the process of green environmental protection and no pollution; the invention of the modifier can greatly enhance the surface activity of silica sand, optimize the adhesion between it and resin and organic binder; the modified silica can maintain stable performance in long time, its application in the cold box coremaking, can significantly reduce the cost in the process of casting sand.
【技术实现步骤摘要】
一种硅砂改性方法
本专利技术涉及矿业生产领域，尤其涉及一种硅砂改性方法。
技术介绍
硅砂的表面状态对整个铸造过程影响很大，因此在和粘结剂混和之前需要对硅砂进行表面处理，一般对硅砂表面处理的方法主要分为物理-机械法和化学法。物理-机械法包括对采集的硅砂进行擦洗、磁选、浮选等，此法主要缺点是提纯效果不佳且耗能大。化学法主要用无机酸和还原剂进行处理，通过此法硅砂性能虽有提升，但是使用的化学试剂较多，易对环境造成污染且成本居高不下。目前，有人尝试采用聚乙烯醇对硅砂表面进行处理，使硅砂性能有一定程度提升，但经过聚乙烯醇改性后硅砂的性能随时间的变化不稳定，且改性过程中受环境影响较大，易产生副作用，反而使硅砂性能下降。
技术实现思路
本专利技术要解决的技术问题是提供一种硅砂的改性方法，采用硅砂改性剂对硅砂进行表面改性，该改性剂原料来源广、成本低且安全环保，能显著强化硅砂表面的活性，改性后硅砂的性能在长时间保持稳定。为解决上述技术问题，本专利技术的技术方案为：一种硅砂改性方法，其创新点在于：包括以下步骤：将硅砂进行去杂烘干，然后预热至76～82℃，置于混砂机中，加入硅砂表面改性剂，混...
【技术保护点】
一种硅砂改性方法，其特征在于：包括以下步骤 ：将硅砂进行去杂烘干，然后预热至 76 ～ 82℃，置于混砂机中，加入硅砂表面改性剂，混合 50 ～ 70s， 得改性硅砂；所述硅砂表面改性剂中各组分所占质量百分比为 ：羧甲基纤维素 3.5 ～ 5％、十二烷基磺酸钾 1.2 ～ 2％、偶联剂 0.6 ～ 1％，其余为水；所述羧甲基纤维素的粘度要求为其质量浓度为 3％的水溶液的粘度在 0.2 ～ 0.4Pa·s 之间；所述偶联剂为γ‑甲基丙烯酰氧基丙基三甲氧基硅烷；所述铸造用硅砂与铸造用硅砂表面改性剂的质量比为 (60 ～ 65):1。
【技术特征摘要】
1.一种硅砂改性方法，其特征在于：包括以下步骤：将硅砂进行去杂烘干，然后预热至76～82℃，置于混砂机中，加入硅砂表面改性剂，混合50～70s，得改性硅砂；所述硅砂表面改性剂中各组分所占质量百分比为：羧甲基纤维素3.5～5％、十二烷基磺酸钾1.2～2％、偶联剂0.6～1％，其余为水；所述羧甲基纤维素的粘度要求为其质量浓度为3％的水溶液的粘度在0.2～0.4Pa·s之间；所述偶联剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷；所述铸造用硅砂与铸造用硅砂表面改性剂的质量比为(...
【专利技术属性】
技术研发人员：施路明，
申请(专利权)人：江苏闽江矿业有限公司，
类型：发明
国别省市：江苏,32