一种提高镁合金强度的处理方法技术
A method to improve the strength of magnesium alloy
The present invention is a treatment method to improve the strength of magnesium alloy. The method comprises the following steps: 1) the cast magnesium alloy materials in liquid nitrogen or static 5min~24h, the cast magnesium alloy after solid solution treatment, plastic deformation after processing in liquid nitrogen, the static 5min~24h; 2) magnesium alloy material after cryogenic treatment removed, placed in the air. Return to room temperature. The invention makes use of the cryogenic treatment process to greatly improve the hardness of the magnesium alloy in the system in a short time. The invention has excellent treatment effect on the magnesium alloy with high content of Al or Sn, so that it can meet the industrial needs better.
【技术实现步骤摘要】
一种提高镁合金强度的处理方法
本专利技术涉及一种提升高Sn或高Al含量镁合金力学性能的热处理方法，特别是涉及一种利用深冷处理提高变形镁合金强度的处理方法。
技术介绍
镁合金作为最轻的金属结构材料，比强度高、抗冲击性能良好，可满足航空航天、汽车及电子产品轻量化的要求，减少能源消耗和环境污染，故成为发达国家与地区工业应用增长最快的材料之一。但是同其他材料相比，目前大部分镁合金的力学性能仍偏低，如何改善其力学性能一直是国内外研究的热点。因此，开发兼具低成本和高性能的镁合金具有广阔的市场前景。众所周知，合金化是提高材料力学性能行之有效的手段。研究表明，镁合金中添加稀土元素(RE)可制备出性能优异的镁合金，但制备工艺复杂和价格偏高等因素极大限制了其大规模应用，所以不含稀土元素的高性能镁合金(如Mg-Sn合金系)日益受到海内外研究者的关注与重视。已有报道均表明Mg-Sn合金体系可进一步通过合适的热处理工艺提高其力学性能，这归因于时效处理析出大量弥散第二相的强化作用，添加Na元素虽可大大缩短到达硬度峰值的时间，但其易在晶界偏聚而恶化材料的塑性(T.T.Sasaki,F.R.El...
【技术保护点】
一种提高镁合金强度的处理方法，其特征为该方法包括以下步骤：1）将铸态镁合金材料放入液氮中静置5min~24h，或者将铸态镁合金材料依次经过固溶处理、塑性变形处理后放入液氮中，静置5min~24h；其中，所述的镁合金材料为含6~10%Al、0.5~6%Sn、0.5~2%Zn，或者含6~10%Sn、0.5~6%Al、0.5~2%Zn，其余为Mg及不可避免的杂质；2）将深冷处理后的镁合金材料取出，置于空气中，自然恢复到室温。
【技术特征摘要】
1.一种提高镁合金强度的处理方法，其特征为该方法包括以下步骤：1）将铸态镁合金材料放入液氮中静置5min~24h，或者将铸态镁合金材料依次经过固溶处理、塑性变形处理后放入液氮中，静置5min~24h；其中，所述的镁合金材料为含6~10%Al、0.5~6%Sn、0.5~2%Zn，或者含6~10%Sn、0.5~6%Al、0.5~2%Zn，其余为Mg及不可避免的杂质；2）将深冷处理后的镁合金材料取出，置于空气中，自然恢复到室温。2.如权利要求1所述的提高镁合金强度的处理方法，其特征...
【专利技术属性】
技术研发人员：余晖，肖海涛，范少达，李丽超，丁俭，夏兴川，宋开红，
申请(专利权)人：河北工业大学，
类型：发明
国别省市：天津,12