一种经济型具有耐腐蚀性能J55无缝管及其制造方法技术
An economical J55 seamless tube with corrosion resistance and its manufacturing method
The invention provides an economical type corrosion resistant performance of J55 seamless pipe and its manufacturing method, the seamless pipe components according to weight percentage are as follows: C:0.28% ~ 0.33%, Si:0.15% ~ 0.40%, Mn:1.30% ~ 1.50%, Cr:0.20% ~ 0.40%, Cu:0.15% ~ 0.25%, Ti:0.01% ~ 0.03%, P = 0.018%, S: 0.010%, the rest is: Iron and unavoidable impurities. The manufacturing methods are as follows: converter billet, refining, vacuum treatment, continuous casting and continuous rolling to get the tube blank. The tube billet is heated to 1200 ~ 1260 C by ring furnace, MPM continuous rolling, after perforation, the temperature is 1160~1200 degrees, and the sizing temperature is 720 ~ 750 C. The invention has uniform organization and good mechanical properties, and the manufacturing process of the product is easy to be realized and economical.
【技术实现步骤摘要】
一种经济型具有耐腐蚀性能J55无缝管及其制造方法
本专利技术属于耐腐蚀材料及无缝钢管领域，尤其涉及具有抗CO2性能的无缝管。
技术介绍
随着我国各大油气田的不断开发，面临的问题和条件也日益变得严峻、苛刻起来，特别是CO2腐蚀问题尤为严重，不仅严重影响了油气的产量，还会造成严重的经济损失。国内外研究表明，CO2腐蚀性极强，采用含有高合金元素的13Cr、22Cr等不锈钢管被认为是抗CO2腐蚀的理想选材，目前也有3Cr钢应用的报道。但含有大量昂贵的元素，极大地增加了钢管的制造成本，从而限制了它们在油气田的广泛应用，而J55钢级油管一般应用于浅井，若加入大量价格昂贵的耐腐蚀合金，不仅投资成本较高，而且对其焊接性能有一定的影响。因此，研究经济型低Cr油管钢，对于降低腐蚀危害，控制开发成本，意义特别重大。《110ksi级高抗CO2腐蚀油套管及其制造方法》(CN102851607A)，该专利通过低碳和氮的微合金化，主要解决了油套管在生产过程中低韧性的问题，但其为高Cr马氏体不锈钢。专利技术“含稀土抗CO2经济型套管材料及其制备方法”(CN103131952A)，该专利通过加入稀...
【技术保护点】
一种经济型具有耐腐蚀性能J55无缝管，其特征在于，该无缝管的成分按重量百分比计如下：C：0.28％～0.33％、Si：0.15％～0.40％、Mn：1.30％～1.50％、Cr：0.20％～0.40％、Cu：0.15％～0.25％、Ti：0.01％～0.03％、P：≤0.018％、S：≤0.010％，其余为铁及不可避免的杂质元素。
【技术特征摘要】
1.一种经济型具有耐腐蚀性能J55无缝管，其特征在于，该无缝管的成分按重量百分比计如下：C：0.28％～0.33％、Si：0.15％～0.40％、Mn：1.30％～1.50％、Cr：0.20％～0.40％、Cu：0.15％～0.25％、Ti：0.01％～0.03％、P：≤0.018％、S：≤0.01...
【专利技术属性】
技术研发人员：陈克东，赵波，解德刚，邸军，藏绍双，常宏伟，郑云龙，谷大伟，
申请(专利权)人：鞍钢股份有限公司，
类型：发明
国别省市：辽宁,21