The invention provides a normalized low temperature of 50 DEG C steel, the steel components according to weight percentage are as follows: C:0.09% ~ 0.15%, Si:0.16% ~ 0.50%, Mn:0.60% ~ 1.18%, Ni:0.10% ~ 0.50%, Mo:0.01% ~ 0.09%, Cr:0.15% ~ 0.30%, V:0.06% ~ 0.10%, Ti:0.015% ~ 0.030%, S = 0.005%, P = 0.008% the rest is Fe and inevitable impurities, Ceq = 0.36. Manufacturing methods: converter smelting, refining, continuous casting, slab slow cooling, cleaning, rolling, heat treatment. The method for producing the low temperature steel, yield strength more than 350MPa, the tensile strength of 500 630MPa, extending rate greater than 25%, the strength is about 15% higher than the same level of 09MnNiDR steel.
【技术实现步骤摘要】
一种正火-50℃低温用钢及其制造方法
本专利技术属于低合金钢制造领域，尤其涉及低温储罐等的建造。
技术介绍
低温用钢主要用于制作储存和运输各类液化气体的设备，包括液化石油气、液化乙烯气、液氨等，低温用钢通常要求具有较高的强度和较好的低温冲击韧性。近年来，随着我国石油、化工行业的快速发展以及全世界范围内对于清洁能源的需求的迅猛增加，此类低温用钢的需求量越来越大。低温用钢包括奥氏体低温钢和铁素体低温钢，铁素体低合金低温钢就是通过在钢中添加少量的Ni、Cr、Mo等合金元素，辅以合适的轧制及热处理工艺，获得理想的显微组织，使钢在较低的制造成本下，具备足够的强度和低温韧性，以及优良的焊接性能。现有技术专利《一种调质低温用钢及其制造方法》(公开号CN102286692A)，公开的调质低温用钢化学成分质量分数为：C：0.04～0.08％，Si：≤0.15％，Mn：1.20～1.60％，P：≤0.015％，S：≤0.003％，Als：≤0.010％，Cu：0.05～0.35％，Ni：0.10～0.40％，Mo：0.10～0.30％，Ti：0.007～0.012％，V：0.020～...
【技术保护点】
一种正火‑50℃低温用钢，其特征在于，该钢板的成分按重量百分比计如下：C：0.09％～0.15％，Si：0.16％～0.50％，Mn：0.60％～1.18％，Ni：0.10％～0.50％，Mo：0.01％～0.09％，Cr：0.15％～0.30％，V：0.06％～0.10％，Ti：0.015％～0.030％，S：≤0.005％，P：≤0.008％，余量为Fe和不可避免的杂质，碳当量应控制在≤0.36，Ceq＝C+Si/24+Mn/6+Ni/40+Cr/5+Mo/4+V/14。
【技术特征摘要】
1.一种正火-50℃低温用钢，其特征在于，该钢板的成分按重量百分比计如下：C：0.09％～0.15％，Si：0.16％～0.50％，Mn：0.60％～1.18％，Ni：0.10％～0.50％，Mo：0.01％～0.09％，Cr：0.15％～0.30％，V：0.06％～0.10％，Ti：0.015％～0.030％，S：≤0.005％，P：≤0.008％，余量为Fe和不可避免的杂质，碳当量应控制在≤0.36，Ceq＝C+Si/24+Mn/6+Ni/40+Cr/5+Mo/4+V/14。2.一种权利要求1所述的正火-50℃低温用钢的制造方法，包括转炉冶...
【专利技术属性】
技术研发人员：朱莹光，侯家平，张宏亮，
申请(专利权)人：鞍钢股份有限公司，
类型：发明
国别省市：辽宁,21