The invention belongs to a method for making antiskid adhesive and its application. Guar gum is used to make the following non slip adhesive conditions, water and guar gum ratio (water powder ratio) range: 150:1 210:1 (v/w), gelatinization temperature range: at room temperature of 90 DEG C, the heating time range: 20 40 min, can be made of guar gum anti slip rubber. The anti slip rubber can be used as bonding material between the packaging carton and packing carton, carton packaging and transport guarantee in the stacking and transportation process of the bond, at the same time, the need to be separated by packing carton, transverse shear force is very small, can be opened without packaging cartons, carton or rarely adhesion between. The advantages of this method are less material, faster speed, easy to operate, easy to popularize and apply.
【技术实现步骤摘要】
瓜儿豆胶制备防滑胶的方法与应用
本专利技术属于淀粉制作防滑胶的
,具体说是通过瓜儿豆胶糊化后制作包装纸箱用的防滑胶,保证在包装纸箱码垛、转运、运输等过程的粘结,同时,在需要将包装纸箱分离时,通过很小的横向剪切力,即可将包装纸箱打开,且没有或者很少纸箱之间的粘连。
技术介绍
瓜儿豆胶防滑胶是指利用瓜儿豆胶通过一定的水粉比、合适的糊化温度及糊化时间,即形成一定黏度的瓜儿豆胶防滑胶。瓜儿豆胶防滑胶是新型材料,主要应用于产品的包装纸箱在生产中纸箱之间相互粘接有一定的强度,保证码垛的高度和稳定性,但同时,包装纸箱之间在分离时,要保证纸箱粘结面的完整性和分离容易,从而减少了传统纸箱之间的塑料薄膜包装材料,节约了包装时间,降低了包装和运输的成本,并且方便分离。因此,瓜儿豆胶防滑胶可以应用于一般的产品包装纸箱,特别是未有光亮面的纸箱之间的码垛、转运、运输等过程的防滑粘结。目前,对传统的包装纸箱防滑处理的方法有:塑料薄膜缠绕法、打包带打包法、进口防滑胶粘结等方法。现有的方法存在如下不足:(1)在生产企业内部的码垛、转运不够方便;(2)包装材料的成本高,如塑料薄膜、打包带等耗材的使用数量较多;(3)包装耗时较长,生产成本增加。
技术实现思路
本专利技术提供一种利用瓜儿豆胶制作防滑胶的方法及其应用,其目的就是体现利用瓜儿豆胶为原材料,通过淀粉糊化制作成为包装纸箱用的防滑胶。本专利技术的目的是通过以下技术方案来实现的:本专利技术的瓜儿豆胶用来制作防滑胶的条件如下,水粉比范围为:150:1-210:1(v/w),糊化加热温度范围为:室温-90℃,加热时间范围为:20-40min, ...
【技术保护点】
瓜儿豆胶制备防滑胶的方法与应用,其特征在于:所述方法水粉比的范围为:150:1‑210:1(v/w)。
【技术特征摘要】
1.瓜儿豆胶制备防滑胶的方法与应用,其特征在于:所述方法水粉比的范围为:150:1-210:1(v/w)。2.其特征在于:糊化加热温度范围为:室温-90℃。3.其特征在于:加热时间范围为...
【专利技术属性】
技术研发人员:贾峰,赵彦海,孙东东,王金水,
申请(专利权)人:河南工业大学,
类型:发明
国别省市:河南,41