The invention relates to a process for using red mud production method of inorganic fiber material, which belongs to the field of comprehensive utilization of red mud, adding curing agent, acidity regulator in the red mud, high temperature melting and coke, make full use of red mud, curing agent, acidity regulator in Si, Ca, Fe, Al, Na, Mg elements of resources, with red mud as the main material for production of inorganic fiber, above the red mud proportion up to 70%, effective governance of red mud pollution, inorganic fiber production reached the level of rock wool economic benefits, environmental benefits, social significant. The process is simple and the production cost is low. It can realize the large-scale production of red mud comprehensive utilization.
【技术实现步骤摘要】
利用赤泥生产无机纤维的工艺方法本专利技术是申请日为2015.10.13，申请号为2015106684305，专利技术名称为“利用赤泥生产无机纤维的工艺方法”的分案申请。
：本专利技术属于赤泥综合利用领域，特别是一种利用赤泥生产无机纤维的工艺方法。
技术介绍
赤泥是铝土矿经“拜耳法”或“烧结法”提出氧化铝后产生的残渣。赤泥的产生量与生产方法及矿石品位有关，一般每生产1吨氧化铝就会产生1-1.7吨的矿渣，这些矿渣因富含氧化铁而呈红褐色，被称之为赤泥，属于有害固体废物，原料品位越低，赤泥产生量越大。中国作为世界4大氧化铝生产国，每年排放的赤泥高达数千万吨。大量的赤泥不能充分有效的利用，目前，氧化铝厂的赤泥处理依然采用建赤泥库坝进行堆放，随着排放量的不断增加，不仅占用了大量的农田，而且对环境产生较大的影响。目前对赤泥的利用一般以提铁处理为主，但从实际运营看，赤泥提铁成本较高，提铁后的粉灰又造成二次污染。提铁后的赤泥作为墙体材料、作路基材料使用，质量需长期进一步检验；作为塑料型材、微晶玻璃板材、赤泥陶粒、普通水泥使用，只能是添加剂，消耗量很少；以前有利用赤泥为辅料和粉煤灰氧...
【技术保护点】
利用赤泥生产无机纤维的工艺方法，其工艺步骤为：(1)以赤泥为主料加入水泥、硅石粉，加水搅拌混合均匀，强力压制成球块状，自然晾干，固化形成球块状物料；(2)球块状物料再与焦碳进行配料，混合均匀，形成半成品物料；(3)所述半成品物料在熔化炉中进行高温熔融，形成熔融液；(4)熔融液上部为无机纤维熔液，无机纤维熔液经离心机甩丝，固化后，形成无机纤维；熔融液下部为铁熔液，进行提铁处理。
【技术特征摘要】
1.利用赤泥生产无机纤维的工艺方法，其工艺步骤为：(1)以赤泥为主料加入水泥、硅石粉，加水搅拌混合均匀，强力压制成球块状，自然晾干，固化形成球块状物料；(2)球块状物料再与焦碳进行配料，混合均匀，形成半成品物料；(3)所述半成品物料在熔化炉中进行高温熔融，形成熔融液；(4)熔融液上部为无机纤维熔液，无机纤维熔液经离心机甩丝，固化后，形成无机纤维；熔融液下部为铁熔液，进行提铁处理。2.根据权利要求1所述的利用赤泥生产无机纤维的工艺方法，其特征在于：赤泥与水泥、硅石粉按1：0.15：0....