单相铌酸钴纳米材料的制备方法技术
Preparation of monophasic cobalt niobate nanomaterials
The invention provides a preparation method of single-phase cobalt niobate nanometer material, which comprises the following steps: five niobium chloride and cobalt chloride according to the stoichiometric ratio of 2:1 dissolved in alcohol solution, obtained solution A; ammonium carbonate dissolved in aqueous solution to obtain B solution; the solution A and B mixed with each other at room temperature, stirring time, suspension liquid; the suspension centrifugal processing to obtain powder; the powder will be dry; dry powder in 700 ~ 1000 8C 6 ~ 12h, the single-phase cobalt niobate nano materials. The single phase cobalt niobate nanomaterials obtained by this method have no heterozygous phase.
【技术实现步骤摘要】
单相铌酸钴纳米材料的制备方法
本专利技术涉及无机材料化学领域，尤其涉及一种单相铌酸钴纳米材料的制备方法。
技术介绍
铌酸盐陶瓷材料具有优异的介电性质，可作为一种微波介质陶瓷，也可以作为多种反应的催化材料，在电子元器件材料、催化材料以及电极材料领域具有良好的应用潜力，引起了人们广泛的研究兴趣。铌酸盐的晶粒尺寸直接影响该材料的性能。目前，大部分的铌酸盐材料均采用高温固相法或者湿化学沉淀法合成。对于高温固相法来说，由于合成的原料多为固相的氧化物或金属粉末，极易造成铌酸盐颗粒长大。对于湿化学沉淀法来说，当采用强碱(含氢氧根)作为沉淀剂时，往往容易引入由碱带来的杂质元素，形成杂质相；另外，氢氧化物沉淀在进行加热形成氧化物的过程中，氢氧化物会发生较为严重的硬团聚，容易造成铌酸盐晶粒的第二次长大。
技术实现思路
鉴于上述技术问题，本专利技术提供一种晶粒尺寸较小的单相铌酸钴纳米材料的制备方法。一种单相铌酸钴纳米材料的制备方法，包括以下步骤：将五氯化铌以及氯化亚钴按照2:1的化学计量比溶解于醇溶液中，获得溶液A；将碳酸铵溶解于水溶液中获得溶液B；将溶液A与溶液B相互混合，室温下搅拌一定...
【技术保护点】
一种单相铌酸钴纳米材料的制备方法，其特征在于，包括以下步骤：将五氯化铌以及氯化亚钴按照2:1的化学计量比溶解于醇溶液中，获得溶液A；将碳酸铵溶解于水溶液中获得溶液B；将溶液A与溶液B相互混合，室温下搅拌一定时间，获得悬浮液；将所述悬浮液进行离心处理获得粉末；将所述粉末进行干燥；将干燥的粉末在700～1000℃煅烧6～12h，获得所述单相铌酸钴纳米材料。
【技术特征摘要】
1.一种单相铌酸钴纳米材料的制备方法，其特征在于，包括以下步骤：将五氯化铌以及氯化亚钴按照2:1的化学计量比溶解于醇溶液中，获得溶液A；将碳酸铵溶解于水溶液中获得溶液B；将溶液A与溶液B相互混合，室温下搅拌一定时间，获得悬浮液；将所述悬浮液进行离心处理获得粉末；将所述粉末进行干燥；将干燥的粉末在700～1000℃煅烧6～12h，获得所述单相铌酸钴纳米材料。2.如权利要求1所述的单相铌酸钴纳米材料的制备方法，其特征在于，所述醇溶液为甲醇、乙醇、丙醇和丁醇的一种或几种。3.如权利要求1所述的单相铌酸钴纳米材料的制备方法，其特征在于，所述醇溶液和水溶液的体积比为2:1～10:1。4.如权利要求1所述的单相铌酸钴纳米材料的制备方法，其特征在于，所述五氯化铌、氯化亚钴以及碳酸铵通过机械搅拌或超声搅拌分别溶解于相应的醇溶液和水溶液中。5.如权利要...
【专利技术属性】
技术研发人员：李勃，高爽，
申请(专利权)人：清华大学深圳研究生院，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。