The invention discloses a method of preparing nitrogen doped manganese molybdate photocatalyst comprises the following steps: 5g ammonium molybdate dissolved in 100 ~ 500mL concentration is 3% ~ 10% in dilute nitric acid, drops into the 40 ~ 120mL concentration is 20 ~ 180g/L by manganese chloride under stirring, adding continue to complete the mixing of 10 ~ 20min, in continuous stirring, 25 DEG C and under conditions of slow access to 0.5 ~ 6L ammonia, finally all reactants to the autoclave PTFE substrate, in the oven at 160 to 180 DEG C for 18 ~ 24h after natural cooling, after centrifugation to solid by ionized water washing and drying to obtain a nitrogen doped manganese molybdate photocatalyst. Through nitrogen doping, the nitrogen doped manganese molybdate photocatalyst with good catalytic effect can be obtained.
【技术实现步骤摘要】
一种氮掺杂钼酸锰光催化剂的制备方法
本专利技术涉及环境污染控制新材料领域,尤其涉及一种氮掺杂钼酸锰光催化剂的制备方法。
技术介绍
随着科技的发展,来自工农业生产中产生的毒害有机污染物严重威胁着环境和人类的健康,寻求一种新型高效的环境治理技术具有重要的意义。光催化技术因其节能、高效、污染物降解彻底、无二次污染优点,目前已成为一种具有重要应用前景的新兴环境治理技术。近年来,新型高效的可见光光催化剂的研制成为光催化技术中的一个重要研究内容,其中具有表面等离子共振效应的光催化材料,因其独特的表面物理化学性质和高效的可见光光催化性能,成为研究的热点之一。钼酸锰纳米材料是一种重要的功能材料,在发光材料、微波材料、磁性器件、传感器件、催化剂等领域有很广阔的应用市场。钼酸锰经过水热反应,可以改善光催化效果。但未改性的钼酸锰的光生电子和空穴负荷率较高,污染物降解率较低。
技术实现思路
本专利技术的目的是为克服现有技术的不足,提供一种氮掺杂钼酸锰光催化剂的制备方法。本专利技术采用的技术方案是依次包括如下步骤:将5g钼酸铵溶解于100~500mL质量百分浓度为3%~10%的稀硝酸中,在搅拌下逐滴滴入40~120mL浓度为20~180g/L的氯化锰,滴加完成后继续搅拌10~20min,再在持续搅拌下,25℃和常压条件下缓慢通入0.5~6L氨气,最后将所有反应物转移到聚四氟乙烯衬底的水热反应釜中,放入烘箱中在160~180℃下反应18~24h后自然冷却,离心后得到固体物经过去离子水洗涤、干燥,即得到一种氮掺杂钼酸锰光催化剂。本专利技术的优点是:经过氮掺杂,可以得到催化效果良好的有机污染 ...
【技术保护点】
一种氮掺杂钼酸锰光催化剂的制备方法,其特征是依次包括如下步骤:将5g钼酸铵溶解于100~500mL质量百分浓度为3%~10%的稀硝酸中,在搅拌下逐滴滴入40~120mL浓度为20~180g/L的氯化锰,滴加完成后继续搅拌10~20min,再在持续搅拌下,25℃和常压条件下缓慢通入0.5~6L氨气,最后将所有反应物转移到聚四氟乙烯衬底的水热反应釜中,放入烘箱中在160~180℃下反应18~24h后自然冷却,离心后得到固体物经过去离子水洗涤、干燥,即得到一种氮掺杂钼酸锰光催化剂。
【技术特征摘要】
1.一种氮掺杂钼酸锰光催化剂的制备方法,其特征是依次包括如下步骤:将5g钼酸铵溶解于100~500mL质量百分浓度为3%~10%的稀硝酸中,在搅拌下逐滴滴入40~120mL浓度为20~180g/L的氯化锰,滴加完成后继续搅拌10~20min,...