本发明专利技术涉及涂料技术领域，特别涉及一种夜光印刷涂料。所述涂料由下述重量配比的各组分组成，丙烯酸树脂20～25份，聚酰胺树脂15～20份，玻璃微粉5～8份，钛粉3～8份，荧光剂15～20份，石英石3～8份，硅酸镁5～10份，滑石粉1～3份，二氧化硅 1～5份。本发明专利技术与现有技术相比的有益效果是：本发明专利技术能够在夜间发光的持续时间长，比现有发光时间多出30%；高亮度持续时间长。

A noctilucent printing coating

The invention relates to the field of coating technology, in particular to a noctilucent printing coating. The coating was by the weight of components, 20 to 25 portions of acrylic resin, polyamide resin 15 ~ 20, 5 ~ 8 glass powder, titanium powder 3 ~ 8, 15 ~ 20 fluorescent agent, quartz stone from 3 to 8, 5 to 10 parts of magnesium silicate, talcum powder 1 ~ 3, 1 ~ 5 silica. Compared with the prior art, the invention has the beneficial effect that the luminous duration of the invention can be longer at night, 30% times higher than the existing luminous time, and the duration of high brightness is long.

【技术实现步骤摘要】
一种夜光印刷涂料
本专利技术涉及涂料
，特别涉及一种夜光印刷涂料。
技术介绍
近年来，越来越多的可用于精细丝网印刷的荧光涂料不断出现。荧光涂料主要用语印刷橱窗陈设、贴花纸、保险杠护挡、工业保险仪器、车身广告、信筏、招贴画（海报）、24英寸海报、记事本、信号旗、杂志封面、请柬、户外广告、布标等。荧光涂料是发光材料，是能够发射光的物质。现有荧光涂料在夜间发光的时间短，高亮度持续时间短，往往达不到用户的预期效果。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种夜光印刷涂料。为实现上述目的，本专利技术采用的技术方案是：本专利技术所述的一种夜光印刷涂料，所述涂料由下述重量配比的各组分组成，丙烯酸树脂20～25份，聚酰胺树脂15～20份，玻璃微粉5～8份，钛粉3～8份，荧光剂15～20份，石英石3～8份，硅酸镁5～10份，滑石粉1～3份，二氧化硅1～5份。本专利技术与现有技术相比的有益效果是：本专利技术能够在夜间发光的持续时间长，比现有发光时间多出30%；高亮度持续时间长。具体实施方式下面结合具体实施例对本专利技术进行详细描述，下述实施例及说明仅用来解释本专利技术，但并不本文档来自技高网...

【技术保护点】
一种夜光印刷涂料，其特征在于：所述涂料由下述重量配比的各组分组成，丙烯酸树脂20～25份， 聚酰胺树脂15～20份，玻璃微粉5～8份，钛粉3～8份，荧光剂15～20份，石英石3～8份，硅酸镁5～10份，滑石粉1～3份，二氧化硅 1～5份。

【技术特征摘要】
1.一种夜光印刷涂料，其特征在于：所述涂料由下述重量配比的各组分组成，丙烯酸树脂20～25份，聚酰胺树脂15～20份，...